Flexural failure mechanism of 2.5D woven SiCf/SiC composites: Combination of acoustic emission, digital image correlation and X-ray tomography
Source abstract
Abstract
Abstract 2.5D woven SiCf/SiC composites are candidate materials for high-temperature components. This work presents the flexural progressive damage behaviors of 2.5D woven SiCf /SiC composites using the combination techniques of acoustic emission (AE), digital image correlation (DIC) and X-ray micro-computed tomography (Micro-CT). 2.5D woven samples with 0° (warp) and 90° (weft) directions and 2D woven laminated samples are experimentally tested via three points bending method. Also, in this process, AE and DIC are employed to monitor the progressive damage process. Subsequently, Micro-CT is utilized to identify the internal damage evolution. The results show that the preform structures and the tested directions both have a significant influence on the mechanical properties and failure mechanisms of 2.5D woven SiC f /SiC composites. Detailly, 2.5D warp samples present the pseudo-ductile fracture, whereas 2.5D weft samples indicate the brittle fracture . Furthermore, the dominant failure mechanisms of 2.5D warp samples are mainly influenced by the bulking warps, whereas those of 2.5D weft samples are controlled by the straight wefts.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Mechanical Behavior of Composites · Advanced Surface Polishing Techniques
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (29)
Show source-provided references
1. Acoustic emission analysis using Bayesian model selection for damage characterization in ceramic matrix composites10.1016/j.jeurceramsoc.2020.03.035 ↗
2. Mechanical properties and real-time damage evaluations of environmental barrier coated SiC/SiC CMCs subjected to tensile loading under thermal gradients10.1016/j.surfcoat.2015.07.042 ↗
3. The design of the fibre-matrix interfacial zone in ceramic matrix composites10.1016/S1359-835X(97)00128-0 ↗
4. Flexural behaviors and microstructures of SiC/SiC composites fabricated by microwave sintering assisted with heat molding process10.1016/j.ceramint.2019.09.259 ↗
5. Microstructure and damage evolution of SiCf/PyC/SiC and SiCf/BN/SiC mini-composites: a synchrotron X-ray computed microtomography study10.1016/j.ceramint.2019.03.004 ↗
6. Damage identification in fiber reinforced titanium matrix composites using acoustic emission10.1016/j.jallcom.2020.153928 ↗
7. Damage development of a woven SiCf/SiC composite during multi-step fatigue tests at room temperature10.1016/j.ceramint.2020.05.270 ↗
8. Acoustic emission pattern recognition on tensile damage process of C/SiC composites using an improved genetic algorithm10.15541/jim20190213 ↗
9. Acoustic emission and X-ray computed microtomography characterization of damage accumulation in a woven Cf/SiC composite10.1016/j.matchar.2019.05.033 ↗
10. Damage monitoring and identification in SiC/SiC minicomposites using combined acousto-ultrasonics and acoustic emission10.1016/j.compositesa.2013.10.010 ↗
11. Combining in-situ synchrotron X-ray microtomography and acoustic emission to characterize damage evolution in ceramic matrix composites10.1016/j.jeurceramsoc.2019.05.027 ↗
12. High-velocity impact behaviors and post-impact tension performance of 2D-C/SiC composite beams10.1016/j.ceramint.2020.02.106 ↗
13. Correlation between failure mechanism and rupture lifetime of 2D-C/SiC under stress oxidation condition based on acoustic emission pattern recognition10.1016/j.jeurceramsoc.2020.06.070 ↗
14. Volumetric assessment of fatigue damage in a SiCf/SiC ceramic matrix composite via in situ X-ray computed tomography10.1016/j.jeurceramsoc.2020.04.037 ↗
15. Damage analysis of 2.5D C/C-SiC composites subjected to fatigue loadings10.1016/j.jeurceramsoc.2019.01.014 ↗
16. Damage characterization of laminated composites using acoustic emission: a review10.1016/j.compositesb.2020.108039 ↗
17. Monitoring tensile fatigue crack growth and fiber failure around a notch in laminate SIC/SIC composites utilizing acoustic emission, electrical resistance, and digital image correlation10.1016/j.jeurceramsoc.2018.08.049 ↗
18. In-situ damage monitoring of a SiC/SiC ceramic matrix composite using acoustic emission and digital image correlation10.1016/j.compstruct.2016.09.040 ↗
19. Full-field strain measurements at the micro-scale in fiber-reinforced composites using digital image correlation10.1016/j.compstruct.2015.12.020 ↗
20. Study of mechanical properties and cracking extension resistance behavior of C/SiC composites by single edge notched beam and digital image correlation techniques10.1016/j.msea.2015.09.101 ↗
21. Damage development during flexural loading of a 5-directional braided C/C-SiC composite, characterized by X-ray tomography and digital volume correlation10.1016/j.ceramint.2018.12.020 ↗
22. In situ observation of mechanical damage within a SiC-SiC ceramic matrix composite10.1016/j.jnucmat.2016.09.007 ↗
23. In situ investigation of failure in 3D braided SiCf/SiC composites under flexural loading10.1016/j.compstruct.2021.114067 ↗
24. Fatigue damage evolution in thick composite laminates: combination of X-ray tomography, acoustic emission and digital image correlation10.1016/j.compscitech.2019.107815 ↗
25. Mechanical behavior of LSI based C/C-SiC composites subjected to flexural loadings10.1016/j.compositesa.2017.01.024 ↗
26. Modeling stress-dependent matrix cracking and stress–strain behavior in 2D woven SiC fiber reinforced CVI SiC composites10.1016/j.compscitech.2006.06.007 ↗
27. Identification of damage mechanisms of carbon fiber reinforced silicon carbide composites under static loading using acoustic emission monitoring10.1016/j.ceramint.2019.04.082 ↗
28. Investigation on tensile properties for 3D C/SiC composites by acoustic emission
29. Bending fatigue behavior in an advanced SiC/SiC ceramic matrix composite component at elevated temperature in air