Texture evolution and temperature-dependent deformation modes in ambient- and cryogenic-rolled nanolayered Zr-2.5Nb

Interface-dominate properties can be strengthened when the interface spacing is further reduced to nanoscale dimensions. To analyze the dominant deformation modes in α-Zr sandwiched by α/β interfaces, a nanolayered Zr-2.5Nb alloy was rolled to various reductions at room temperature (RT) and near-liquid-nitrogen temperature (LNT). The α/β lamellar structures are refined significantly when rolling reduction exceeds 25% at both RT and LNT rolling. We show that the alloy is remarkably formable at both RT and LNT, as indicated by homogeneous deformation with no shear banding detected. Based on a combination of microstructural analysis, texture measurements and multi-scale polycrystal model simulations, two types of tensile {1 1 ¯ 02}< 1 ¯ 101> and { 1 ¯ 1 ¯ 21}<11 2 ¯ 6> twins were found to form at LNT rolling and expand until they reoriented all α-Zr lamellae in the same colony to the twin orientation. In addition, the high density of α/β interfaces substantially enhances the activity of pyramidal dislocations in α-Zr during both RT and LNT rolling, eventually tilting the axis of α-Zr nearly parallel to the normal direction of the as-rolled sample. The higher fraction slip activity of dislocations and deformation twins accommodate deformation along direction in α-Zr, increasing the formability of this ultra-strong nanolayered Zr-2.5Nb alloy.