Orientation-dependent transport properties of Cu3Sn

Cu ₃ Sn, a well-known intermetallic compound with a high melting temperature and thermal stability, has found numerous applications in microelectronics, 3D printing, and catalysis. However, the relationship between the material`s thermal conductivity anisotropy and its complex anti-phase boundary superstructure is not well understood. Here, frequency domain thermoreflectance was used to map the thermal conductivity variation across the surface of arc-melted polycrystalline Cu ₃ Sn. Complementary electron backscatter diffraction and transmission electron microscopy revealed the thermal conductivity in the principal a, b, and c orientations to be 57.6, 58.9, and 67.2 W/m-K, respectively. Density functional theory calculations for several Cu ₃ Sn superstructures helped examine thermodynamic stability factors and evaluate the direction-resolved electron transport properties in the relaxation time approximation. The analysis of computed temperature- and composition-dependent free energies suggests metastability of the known long-period Cu ₃ Sn superstructures while the transport calculations indicate a small directional variation in the thermal conductivity. The ∼15% anisotropy measured and computed in this study is well below previously reported experimental values for samples grown by liquid-phase electroepitaxy.