Size-dependent quasi Brittle–Ductile transition of single crystalline alpha-alumina particles during microcompression tests
Source abstract
Abstract
Abstract Dense ceramic coatings can be fabricated through the kinetic impaction of fine solid particles at room temperature without any heat assistance or binder, and such a coating process is known as aerosol deposition (AD). In this process, solid ceramic particles that are generally fragile exhibit plastic deformation when they are refined; this is the key to the deposition and densification of ceramic coatings in AD. However, previous work has failed to address the transition criteria related to the size of ceramic particles during plastic deformation; the size is significantly associated with their fracture strength and strain. To eliminate the grain boundary effect, single crystalline alpha-alumina particles were selected and their strength and strain before fracture were systematically measured in a quasi-static compression test. The fracture strength of the alumina particles increased when the particle size decreased, and the particles exhibited quasi-plastic deformation when the fracture strength reached the compressive strength of alumina. This size-dependent brittle–ductile transition of ceramic materials in compression implies that the intragrain plastic deformation of ceramic particles can be attributed to the solid particle deposition. Thus, appropriately designing the intra grain architecture in ceramic particles may allow highly efficient deposition and further densification in AD.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Particle Dynamics in Fluid Flows · High-Temperature Coating Behaviors
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (46)
Show source-provided references
1. Brittle failure in compression: Splitting faulting and brittle-ductile transition10.1098/rsta.1986.0101 ↗
2. Superplastic nanofibrous slip zones control seismogenic fault friction10.1126/science.1259003 ↗
3. A new technology for machining brittle materials10.1115/1.2899676 ↗
4. The impossibility of comminuting small particles by compression10.1038/272710a0 ↗
5. Microstructure and electrical properties of lead zirconate titanate (Pb(Zr52/Ti48)O3) thick films deposited by aerosol deposition method10.1143/JJAP.38.5397 ↗
6. Room temperature impact consolidation (RTIC) of fine ceramic powder by aerosol deposition method and applications to microdevices10.1007/s11666-008-9163-7 ↗
7. An overview of the aerosol deposition method: process fundamentals and new trends in materials applications, J
8. Promotion of knowledge and technology transfer towards innovative manufacturing process: case study of new hybrid coating process10.20965/ijat.2019.p0419 ↗
9. Aerosol deposition of ceramic thick films at room temperature: densification mechanism of ceramic layers10.1111/j.1551-2916.2006.01030.x ↗
10. The 2016 thermal spray roadmap10.1007/s11666-016-0473-x ↗
11. Alumina thick films as integral substrates using aerosol deposition method10.1143/JJAP.43.5414 ↗
12. Substrate hardness dependency on properties of Al2O3 thick films grown by aerosol deposition10.1016/j.surfcoat.2012.08.012 ↗
13. Antibacterial and water purification activities of self-assembled honeycomb structure of aerosol deposited titania film10.1021/es3037252 ↗
14. Plasma-resistant dense yttrium oxide film prepared by aerosol deposition process10.1111/j.1551-2916.2007.01738.x ↗
15. Piezoelectric properties and poling effect of Pb(Zr, Ti)O3 thick films prepared for microactuators by aerosol deposition10.1063/1.1309029 ↗
16. Hexagonal to cubic crystal structure transformation during aerosol deposition of aluminum nitride10.1016/j.jcrysgro.2004.11.082 ↗
17. Cubic aluminum nitride transformed under reduced pressure using aerosol deposition method10.1111/j.1551-2916.2005.00215.x ↗
18. Microstructure evolution of titanium nitride film during vacuum kinetic spraying,10.1111/jace.12101 ↗
19. Compression test system for a single submicrometer particle10.1063/1.2038187 ↗
20. J. Akedo, Aerosol deposition (AD) process: The basic and applications - novel ceramic coating technology with room temperature impact consolidation (RTIC) (in japanese), CMC Publishing Co., Ltd., 2008.
21. Effect of process for producing Al2O3 particles on deposition efficiency in aerosol deposition method10.2109/jcersj2.122.110 ↗
22. Room temperature deformation mechanisms of alumina particles observed from in situ micro-compression and atomistic simulations10.1007/s11666-015-0295-2 ↗
23. Rapid determination of the tensile strength of rocks with irregular test pieces
24. One-dimensional compression behaviour of uniformly graded sand related to single particle crushing strength10.3208/sandf.41.2_39 ↗
25. Splat morphology of yttria-stabilized zirconia droplet deposited via hybrid plasma spraying10.1007/s11666-009-9460-9 ↗
26. A statistical distribution function of wide applicability10.1115/1.4010337 ↗
27. A practical and systematic review of weibull statistics for reporting strengths of dental materials10.1016/j.dental.2009.09.006 ↗
28. Shock-induced plasticity and fragmentation phenomena during alumina deposition in the vacuum kinetic spraying process10.1016/j.scriptamat.2014.12.008 ↗
29. Investigating the effect of applied strain rate in a single breakage event10.1016/j.mineng.2016.09.010 ↗
30. The local strength of individual alumina particles10.1016/j.jmps.2017.08.005 ↗
31. Fabrication and deformation of three-dimensional hollow ceramic nanostructures10.1038/nmat3738 ↗
32. An improved loop test for experimentally approaching the intrinsic strength of alumina nanoscale whiskers10.1088/0957-4484/24/28/285703 ↗
33. S.J. Schneider, R.W. Rice, The science of ceramic machining and surface finishing: Proceedings, US Department of Commerce, 1972.10.6028/NBS.SP.348 ↗
34. Evaluated material properties for a sintered alpha-alumina10.1111/j.1151-2916.1997.tb03074.x ↗
35. Richerson · 2005
36. Plasticity and fracture of sapphire at room temperature: Load-controlled microcompression of four different orientations10.1016/j.ceramint.2013.07.121 ↗
37. Brittle-to-ductile transition in uniaxial compression of silicon pillars at room temperature10.1002/adfm.200900418 ↗
38. Mechanical properties and deformation of cubic silicon carbide micropillars in compression at room temperature10.1111/j.1551-2916.2012.05346.x ↗
39. Transition from a strong-yet-brittle to a stronger-and-ductile state by size reduction of metallic glasses10.1038/nmat2622 ↗
40. Sample dimensions influence strength and crystal plasticity10.1126/science.1098993 ↗
41. Plasticity of micrometer-scale single crystals in compression10.1146/annurev-matsci-082908-145422 ↗
42. Uniaxial compression of silicon nanoparticles: an atomistic study on the shape and size effects10.1016/j.actamat.2018.07.063 ↗
43. Ultrahigh strength of dislocation-free ni3al nanocubes10.1002/smll.201102603 ↗
44. Real time tem observation of alumina ceramic nano-particles during compression10.1016/j.jeurceramsoc.2012.02.029 ↗
45. Texture development of α-Al2O3 ceramic coatings by aerosol deposition10.2320/matertrans.M2016213 ↗
46. Material hardness at strain rates beyond 106 s−1 via high velocity microparticle impact indentation10.1016/j.scriptamat.2019.10.032 ↗