Jinming Liu, Guannan Guo, Xiaowei Zhang, Fan Zhang, Bin Ma, Jian-Ping Wang

Acta Materialia· Volume 184
Publisher page

Abstract

Magnets with a low-temperature coefficient of coercivity (TCC) have various applications in a varying temperature environment. Rare-earth magnets like NdFeB are widely used, but they usually have a large negative TCC. Here, it is first experimentally demonstrated that α″-Fe 16N 2 foils, as a candidate for rare-earth-free magnets, have an ultralow positive TCC (0.4 Oe/K) from 300 K to 425 K. It is two orders of magnitude smaller than that of the commercial NdFeB magnets in this temperature range. The α″-Fe 16N 2 foils are made from as-rolled iron foils (25 µm) by a low-temperature nitridation process (< 473 K). The microstructure of these iron foils is tuned before the nitridation by a combined oxidation and reduction process to induce pores and defects that could significantly enhance the diffusivity of nitrogen atoms in the foils. The fabricated α″-Fe 16N 2 foils exhibit the specific saturation magnetization up to 222 emu/g at 300 K (reduced iron foils ~ 205 emu/g) and the coercivity 1.1 kOe. The synthesized α″-Fe 16N 2 foils have an ultralow TCC and a high saturation magnetization besides its usages of low-cost and environment-friendly raw materials. These combined unique features make α″-Fe 16N 2 a promising rare-earth-free alternative for many applications required less temperature dependence of magnetic properties.
Source: expertdata · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Magnetic Properties of Alloys · Magnetic properties of thin films · Hydrogen Storage and Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (48)

Show source-provided references
1. Performance comparison of motors fitted with magnet-to-magnet recycled or conventionally manufactured sintered NDFEB10.1016/j.jmmm.2018.04.034 ↗
2. Effects of Ag on the magnetic and mechanical properties of sintered NDFEB permanent magnets10.1016/j.jmmm.2019.04.071 ↗
3. Opportunities and challenges for a sustainable energy future10.1038/nature11475 ↗
4. Permanent magnet applications10.1016/S0304-8853(02)00335-9 ↗
5. Costs, substitution, and material use: the case of rare earth magnets10.1021/acs.est.7b05495 ↗
6. Rare-earth-free propulsion motors for electric vehicles: a technology review10.1016/j.rser.2015.12.121 ↗
7. Current progress and future challenges in rare-earth-free permanent magnets10.1016/j.actamat.2018.07.049 ↗
8. J.P Wang, Environment-friendly bulk Fe16N2 permanent magnet: Review and perspective, J. Magn. Magn. Mater. doi10.1016/j.jmmm.2019.165962.
9. Nitriding and martensitic phase transformation of the copper and boron doped iron nitride magnet10.1016/j.actamat.2019.01.034 ↗
10. Theory of giant saturation magnetization in α″-Fe16N2 : role of partial localization in ferromagnetism of 3d transition metals10.1088/1367-2630/12/6/063032 ↗
11. Fabrication of Fe16N2films by sputtering process and experimental investigation of origin of giant saturation magnetization in Fe16N210.1109/TMAG.2011.2170156 ↗
12. Synthesis, morphology, thermal stability and magnetic properties of α ″ -Fe16N2 nanoparticles obtained by hydrogen reduction of γ -Fe2O3 and subsequent nitrogenation10.1016/j.actamat.2016.10.061 ↗
13. Perpendicular uniaxial magnetic anisotropy of Fe/Sub 16/N/sub 2/[001]single crystal films grown by molecular beam epitaxy10.1109/20.801054 ↗
14. GMR effect in Co-Cu microwires10.3938/jkps.62.1940 ↗
15. α″-Fe16N2 compound based permanent magnet with 20MGOe magnetic energy product for next generation rare-earth-free magnet
16. Heavy‐Metal‐Free, low‐damping, and non‐interface perpendicular Fe16N2 thin film and magnetoresistance device10.1002/pssr.201900089 ↗
17. The occurrence and the crystal structure of formula-iron nitride; a new type of interstitial alloy formed during the tempering of Nitrogen-Martensite
18. Giant magnetic anisotropy in tetragonal FeCo alloys10.1103/PhysRevLett.93.027203 ↗
19. Iron nanoparticles with tunable tetragonal structure and magnetic properties
20. Synthesis of iron nitrides FexN (x: 2, 2-3, 4, 16/2) by nitrogenizing .ALPHA.-Fe in Ammonia Gas, and magnetic properties of the bulk sample of Fe16N210.2497/jjspm.46.151 ↗
21. Magnetic properties of Fe16N2 fine particles10.3379/jmsjmag.25.927 ↗
22. Gas phase preparation of spherical core–shell α′′-Fe16N2/SiO2 magnetic nanoparticles10.1039/c3nr06867f ↗
23. Effect of oxidation on α″-Fe16N2 phase formation from plasma-synthesized spherical core–shell α-Fe/Al2O3 nanoparticles10.1016/j.jmmm.2014.12.015 ↗
24. Preparation of an α″-Fe16N2 Magnet via a ball milling and shock compaction approach
25. Synthesis of Fe16N2 compound free-standing foils with 20MGOe magnetic energy product by nitrogen ion-implantation10.1038/srep25436 ↗
26. Magnetic materials and devices for the 21st century: stronger, lighter, and more energy efficient10.1002/adma.201002180 ↗
27. Positive temperature coefficient of coercivity in Sm 1−x Dy x (Co 0.695 Fe 0.2 Cu 0.08 Zr 0.025) 7.2 magnets with spin-reorientation-transition cell boundary phases
28. Practical aspects of modern and future permanent magnets10.1146/annurev-matsci-070813-113457 ↗
29. A new class of Sm-TM magnets for operating temperatures up to 550°C10.1109/20.908807 ↗
30. Challenge to the synthesis of α’’-Fe16N2 compound nanoparticle with high saturation magnetization for rare earth free new permanent magnetic material10.7567/APEX.6.073007 ↗
31. FeNi and Fe16N2 magnets prepared using leaching10.2320/matertrans.M2019019 ↗
32. Facile synthesis of single-phase spherical α″-Fe16N2 /Al2O3 core-shell nanoparticles via a gas-phase method10.1063/1.4798959 ↗
33. Effect of magnetic field strength on the alignment of α′′-Fe16N2 nanoparticle films10.1039/C5NR07859H ↗
34. Nitriding iron at lower temperatures10.1126/science.1080216 ↗
35. Synthesis of α′′-Fe16N2 ribbons with a porous structure10.1039/C9NA00008A ↗
36. Low-temperature extension of the lehrer diagram and the iron-nitrogen phase diagram10.1007/s11661-002-0380-2 ↗
37. High-temperature oxidation of pure Fe and the ferritic steel 2.25Cr1Mo10.1590/S1516-14392005000400002 ↗
38. Effect of magnetic fields on the formation of Fe16N2 precipitates in Fe-N alloys10.1016/0921-5093(91)90274-Q ↗
39. 9 T high magnetic field annealing effects on Fen bulk sample10.1063/1.4868493 ↗
40. Measurement of effective magnetic anisotropy of nanocrystalline Fe‐Cu‐Nb‐Si‐B soft magnetic alloys10.1063/1.355078 ↗
41. Fabrication of Heuslar Fe[Sub 3]Si nanoparticles10.1063/1.3074135 ↗
42. Effect of the morphology on the mechanisms of the magnetization reversal of multilayered thin Co/Pd films10.1134/S1063783416110160 ↗
43. Angular dependence of coercive field in (Sm,Zr)(Co,Cu,Fe)z alloys10.1016/0304-8853(95)00992-2 ↗
44. Random anisotropy in amorphous ferromagnets10.1063/1.324881 ↗
45. Effect of exchange interactions on the coercivity of SmCo5 nanoparticles made by cluster beam deposition10.1002/adfm.201201353 ↗
46. Shape of temperature dependence of spontaneous magnetization of ferromagnets: quantitative analysis10.1103/PhysRevLett.94.107204 ↗
47. Y. Sugita, K. Mitsuoka, M. Komuro, H. Hoshiya, Y. Kozono, M. Hanazono, Giant magnetic moment and other magnetic properties of epitaxially grown Fe16N2 single-crystal films (invited), 70 (1991) 5977–5982.10.1063/1.350067 ↗
48. Low-temperature ferromagnetism in (Ga, Mn)N: ab initio calculations10.1103/PhysRevB.70.201202 ↗