Synthesis and pseudocapacitive studies of composite films of polyaniline and manganese oxide nanoparticles

Abstract We report the synthesis and pseudocapacitive studies of a composite film (PANI-ND-MnO 2 ) of polyaniline (PANI) and manganese oxide (MnO 2 ) nanoparticles. To enhance the interaction of MnO 2 and PANI, the surfaces of MnO 2 nanoparticles were modified by a silane coupling reagent, triethoxysilylmethyl N-substituted aniline (ND42). The composite film was obtained via controlled electro-co-polymerization of aniline and N-substituted aniline grafted on surfaces of MnO 2 nanoparticles (ND-MnO 2 ) on a carbon cloth in a electrolyte of 0.5 M H 2 SO 4 and 0.6 M (NaPO 3 ) 6 . In comparison to similarly prepared PANI film, the incorporation of MnO 2 nanoparticles substantially increases the effective surface area of the film by reducing the size of rod-like PANI aggregates and avoiding the entanglement of these PANI nanorods. Significantly, we observed significant enhancement of specific capacitance in PANI-ND-MnO 2 film compared to PANI–MnO 2 film prepared in a similar condition, indicating that the presence of the coupling reagent can improve the electrochemical performance of PANI composite film. A symmetric model capacitor has been fabricated by using two PANI-ND-MnO 2 nanocomposite films as electrodes. The PANI-ND-MnO 2 capacitor showed an average specific capacitance of ∼80 F g −1 and a stable coulombic efficiency of ∼98% over 1000 cycles. The results demonstrated that PANI-ND-MnO 2 nanocomposites are promising materials for supercapacitor electrode and the importance of designing and manipulating the interaction between PANI and MnO 2 for fundamentally improving capacitive properties.