Capacity fade of LiAlyNi1−x−yCoxO2 cathode for lithium-ion batteries during accelerated calendar and cycle life tests (surface analysis of LiAlyNi1−x−yCoxO2 cathode after cycle tests in restricted depth of discharge ranges)

Abstract Cycle performance at 60 °C for a Li Al 0.10 Ni 0.76 Co 0.14 O 2 (NCA) cathode/graphite cell was greatly improved when a DOD range in charge–discharge cycling (ΔDOD) was restricted. The deterioration mechanism was analyzed by X-ray photoelectron spectroscopy (XPS), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and scanning transmission electron microscopy-electron energy-loss spectroscopy (STEM-EELS). Only after the cycle test in the ΔDOD of 0–100%, many micro-cracks were generated in the inter-surface between the primary particles which aggregated to form the secondary particles, and a NiO-like resistance layer with Fm3m rock salt structure was formed on each primary particle which was contact with other primary particles and electrolyte. It can be concluded that the lack of contact between the primary particles with the micro-crack generation and the formation of the new resistance layer are responsible for the capacity fading and the rise in impedance during charge–discharge cycle in the wide ΔDOD.