Preparation and characterization of biodegradable scaffolds of poly(lactide-co-glycolide) 50:50 and hydroxyapatite for dental applications
Source abstract
Abstract
In the present study, biodegradable scaffolds of poly(lactide-co-glycolide) PLGA 50:50 with acidic microclimate controlling additives were prepared and characterized for their degradation behavior, physical, and mechanical properties. Results indicate that scaffolds with acidic microclimate controlling additives undergo degradation without large variation in pH of the surrounding medium. Results also indicated that microclimate controlling additives did not significantly alter the physical and mechanical properties of the scaffolds. From the results, it can be concluded that PLGA 50:50 scaffolds with acidic microclimate controlling additives can be used as root replicas after the tooth extraction.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Bone Tissue Engineering Materials · biodegradable polymer synthesis and properties · Dental Implant Techniques and Outcomes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (46)
Show source-provided references
1. 10.1902/jop.2004.75.6.90210.1902/jop.2004.75.6.902 ↗
2. 10.1902/jop.2008.07047610.1902/jop.2008.070476 ↗
3. 10.1563/1548-1336(2008)34[97:IPIESA]2.0.CO;210.1563/1548-1336(2008)34[97:IPIESA]2.0.CO;2 ↗
4. Irinakis T · J. Can. Dent. Assoc · 2006 · 72 · 917
5. Parikh SN · J. Postgrad. Med · 2002 · 48 · 142
6. Serino G · Clin. Oral Implants Res · 2008 · 19 · 2610.1111/j.1600-0501.2007.01311.x ↗
7. 10.1034/j.1600-0501.2003.00970.x10.1034/j.1600-0501.2003.00970.x ↗
8. 10.1111/j.1600-051X.2005.00696.x10.1111/j.1600-051X.2005.00696.x ↗
9. 10.1016/S0142-9612(96)00075-010.1016/S0142-9612(96)00075-0 ↗
10. 10.1053/j.otsm.2004.07.01510.1053/j.otsm.2004.07.015 ↗
11. 10.1016/S0169-409X(97)00048-310.1016/S0169-409X(97)00048-3 ↗
12. 10.1016/S0142-9612(01)00101-610.1016/S0142-9612(01)00101-6 ↗
13. 10.1016/j.jconrel.2005.05.02410.1016/j.jconrel.2005.05.024 ↗
14. 10.1016/j.ijpharm.2008.02.00410.1016/j.ijpharm.2008.02.004 ↗
15. 10.1016/j.tripleo.2003.10.01310.1016/j.tripleo.2003.10.013 ↗
16. 10.1902/jop.2000.71.6.101510.1902/jop.2000.71.6.1015 ↗
17. 10.1902/jop.2003.74.7.96510.1902/jop.2003.74.7.965 ↗
18. 10.1902/jop.1996.67.4.39010.1902/jop.1996.67.4.390 ↗
19. 10.1111/j.1600-051X.1998.tb02378.x10.1111/j.1600-051X.1998.tb02378.x ↗
20. Brkovic BMB · J. Can. Dent. Assoc · 2008 · 74 · 513
21. 10.1902/jop.2002.73.1.9410.1902/jop.2002.73.1.94 ↗
22. 10.1902/jop.2004.75.5.66310.1902/jop.2004.75.5.663 ↗
23. 10.1111/j.1708-8208.2007.00067.x10.1111/j.1708-8208.2007.00067.x ↗
24. Nair PNR · Eur. Cells Mater · 2004 · 7 · 47
25. 10.1177/088532820605416710.1177/0885328206054167 ↗
26. Gunatillake PA · Eur. Cells Mater · 2003 · 5 · 110.22203/eCM.v005a01 ↗
27. 10.1016/j.compscitech.2005.04.05110.1016/j.compscitech.2005.04.051 ↗
28. 10.1016/S0142-9612(01)00382-910.1016/S0142-9612(01)00382-9 ↗
29. 10.1002/(SICI)1097-4636(19970315)34:4<531::AID-JBM13>3.0.CO;2-F10.1002/(SICI)1097-4636(19970315)34:4<531::AID-JBM13>3.0.CO;2-F ↗
30. Mobedi H · Iran. Polym. J · 2006 · 15 · 31
31. 10.1016/j.jconrel.2006.11.02310.1016/j.jconrel.2006.11.023 ↗
32. 10.1016/j.ijpharm.2008.11.01710.1016/j.ijpharm.2008.11.017 ↗
33. 10.1016/j.biomaterials.2005.08.01610.1016/j.biomaterials.2005.08.016 ↗
34. 10.1002/(SICI)1097-4636(19990315)44:4<446::AID-JBM11>3.0.CO;2-F10.1002/(SICI)1097-4636(19990315)44:4<446::AID-JBM11>3.0.CO;2-F ↗
35. 10.1023/A:100751342533710.1023/A:1007513425337 ↗
36. 10.1002/1097-4636(200102)54:2<284::AID-JBM16>3.0.CO;2-W10.1002/1097-4636(200102)54:2<284::AID-JBM16>3.0.CO;2-W ↗
37. 10.1016/j.biomaterials.2003.09.03310.1016/j.biomaterials.2003.09.033 ↗
38. 10.1016/j.actbio.2005.03.00410.1016/j.actbio.2005.03.004 ↗
39. 10.1016/j.biomaterials.2007.06.02910.1016/j.biomaterials.2007.06.029 ↗
40. Gogolewski S · Eur. Cells Mater · 2001 · 1 · 54
41. 10.1016/j.actbio.2007.10.00610.1016/j.actbio.2007.10.006 ↗
42. 10.1016/j.polymdegradstab.2009.11.03910.1016/j.polymdegradstab.2009.11.039 ↗
43. 10.1038/7191610.1038/71916 ↗
44. 10.1016/S0141-3910(02)00404-410.1016/S0141-3910(02)00404-4 ↗
45. 10.1016/j.compscitech.2003.09.00110.1016/j.compscitech.2003.09.001 ↗
46. 10.1016/j.polymertesting.2005.07.01310.1016/j.polymertesting.2005.07.013 ↗