A multi-scale correlative investigation of ductile fracture

M. Daly, T.L. Burnett, E.J. Pickering, O.C.G. Tuck, F. Léonard, R. Kelley, P.J. Withers, A.H. Sherry

Acta Materialia· Volume 130

Abstract

The use of novel multi-scale correlative methods, which involve the coordinated characterisation of matter across a range of length scales, are becoming of increasing value to materials scientists. Here, we describe for the first time how a multi-scale correlative approach can be used to investigate the nature of ductile fracture in metals. Specimens of a nuclear pressure vessel steel, SA508 Grade 3, are examined following ductile fracture using medium and high-resolution 3D X-ray computed tomography (CT) analyses, and a site-specific analysis using a dual beam plasma focused ion beam scanning electron microscope (PFIB-SEM). The methods are employed sequentially to characterise damage by void nucleation and growth in one volume of interest, allowing for the imaging of voids that ranged in size from less than 100 nm to over 100 μm. This enables the examination of voids initiated at carbide particles to be detected, as well as the large voids initiated at inclusions. We demonstrate that this multi-scale correlative approach is a powerful tool, which not only enhances our understanding of ductile failure through detailed characterisation of microstructure, but also provides quantitative information about the size, volume fractions and spatial distributions of voids that can be used to inform models of failure. It is found that the vast majority of large voids nucleated at MnS inclusions, and that the volume of a void varied according to the volume of its initiating inclusion raised to the power 3/2. The most severe voiding was concentrated within 500 μm of the fracture surface, but measurable damage was found to extend to a depth of at least 3 mm. Microvoids associated with carbides (carbide-initiated voids) were found to be concentrated around larger inclusion-initiated voids at depths of at least 400 μm. Methods for quantifying X-ray CT void data are discussed, and a procedure for using this data to calibrate parameters in the Gurson-Tvergaard Needleman (GTN) model for ductile failure is also introduced.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Metal Forming Simulation Techniques · Microstructure and mechanical properties · Metallurgy and Material Forming

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (40)

Show source-provided references
1. Recent advances in X-ray microtomography applied to materials10.1179/174328008X277803 ↗
2. Quantitative X-ray tomography10.1179/1743280413Y.0000000023 ↗
3. Damage quantification in aluminium alloys using in situ tensile tests in X-ray tomography10.1016/j.engfracmech.2011.07.004 ↗
4. Application of 3D X-ray tomography to enhance the calibration of ductile fracture models
5. Investigation of creep damage in advanced martensitic chromium steel weldments using synchrotron X-ray micro-tomography and EBSD10.1179/1743284714Y.0000000621 ↗
6. Bulk evaluation of ductile damage development using high resolution tomography and laminography10.1016/j.crhy.2011.12.009 ↗
7. Damage observation in a high-manganese austenitic TWIP steel by synchrotron radiation computed tomography10.1016/j.scriptamat.2010.08.042 ↗
8. Multiscale 3D analysis of creep cavities in AISI type 316 stainless steel10.1179/1743284714Y.0000000639 ↗
9. The power of correlative microscopy: multi-modal, multi-scale, multi-dimensional10.1016/j.sbi.2011.06.010 ↗
10. Correlative tomography10.1038/srep04711 ↗
11. Rogers · 1960 · 498
12. An investigation of the PlasticFracture of AISI 4340 and 18 Nickel–200 Grade maraging steels10.1007/BF02646633 ↗
13. On the mechanisms of ductile failure in high-strength steels subjected to multi-axial stress-states10.1016/0022-5096(76)90024-7 ↗
14. An extended model for void growth and coalescence10.1016/S0022-5096(00)00019-3 ↗
15. Cavity formation from inclusions in ductile fracture of A508 steel10.1007/BF02648336 ↗
16. Continuum theory of ductile rupture by void nucleation and growth: Part I—yield criteria and flow rules for porous ductile media10.1115/1.3443401 ↗
17. Influence of voids on shear band instabilities under plane strain conditions10.1007/BF00036191 ↗
18. On localization in ductile materials containing spherical voids10.1007/BF00015686 ↗
19. Analysis of cup-cone fracture in a round tensile bar10.1016/0001-6160(84)90213-X ↗
20. Void nucleation effects in biaxially-stretched sheets10.1115/1.3224807 ↗
21. A computational approach to ductile crack growth under large scale yielding conditions10.1016/0022-5096(94)00069-H ↗
22. A new failure criterion for the gurson-tvergaard dilational constitutive model10.1007/BF00032450 ↗
23. Numerical modeling of ductile crack growth in 3-d using computational cell elements10.1007/BF00017864 ↗
24. A view on ductile-fracture modelling10.1046/j.1460-2695.1998.00077.x ↗
25. Micro-mechanical modelling of ductile damage and tearing - results of a european numerical round robin10.1046/j.1460-2695.2002.00468.x ↗
26. A ductile fracture analysis using a local damage model10.1016/j.ijpvp.2007.09.003 ↗
27. ASTM · 2004
28. ESIS TC1 Subcommittee on Fracture Mechanics Testing Standards · 1992
29. Large volume serial section tomography by Xe plasma FIB dual beam microscopy10.1016/j.ultramic.2015.11.001 ↗
30. Ductile crack growth - I. A numerical study using computational cells with microstructurally-based length scales10.1016/0022-5096(94)00064-C ↗
31. Identification of gurson–tvergaard material model parameters via kalman filtering technique. I. Theory10.1023/A:1007602106711 ↗
32. Identification of material parameters of the gurson–tvergaard–needleman model by combined experimental and numerical techniques10.1016/j.commatsci.2004.09.010 ↗
33. Calibration procedures for a computational model of ductile fracture10.1016/j.engfracmech.2009.10.007 ↗
34. Ductile Fracture of A 508 Cl 3 steel in relation with inclusion content: the benefit of the local approach of fracture and continuum damage mechanics10.1016/0029-5493(87)90235-4 ↗
35. Application of local damage models to the numerical analysis of ductile rupture10.1111/j.1460-2695.1989.tb00527.x ↗
36. Micromechanism of ductile fracture initiation - void nucleation and growth
37. Prediction of ductile fracture initiation using micromechanical analysis10.1016/S0013-7944(03)00013-4 ↗
38. Comparison between a quantitative micrscope and chemical methods for assessment of non-metallic inclusions
39. 3D chemical imaging in the laboratory by hyperspectral X-ray computed tomography10.1038/srep15979 ↗
40. Non-destructive mapping of grain orientations in 3D by laboratory X-ray microscopy10.1038/srep14665 ↗