Influence of impurities and deformation temperature on the saturation microstructure and ductility of HPT-deformed nickel
Source abstract
Abstract
Ni with different purities between 99.69 and 99.99 wt.% was deformed by high-pressure torsion (HPT) to high strains, where no further refinement of the microstructure is observed. The HPT deformation temperature varied between -196 and 400 °C. Both impurities and temperature significantly affect the lower limit of the grain size obtained by HPT. In the investigated samples, carbon was the most important impurity element in controlling the limit of grain refinement. The decrease in grain size due to an increase in the carbon content from 0.008 to 0.06 wt.% for HPT-deformed Ni samples at room temperature enhanced the ultimate tensile strength from 1000 to 1700 MPa. Surprisingly, the carbon content did not deteriorate the ductility, defined as the reduction in area, which is mainly limited by the total amount of impurities besides carbon. Furthermore, the deformation temperature dependency on ductility was not very pronounced and only visible for deformation temperatures above 200 °C.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Microstructure and mechanical properties · Aluminum Alloy Microstructure Properties · Microstructure and Mechanical Properties of Steels
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Pippan · Ann Rev Mater Res · 2010 · 40 · 31910.1146/annurev-matsci-070909-104445 ↗
2. Valiev · Prog Mater Sci · 2000 · 45 · 10310.1016/S0079-6425(99)00007-9 ↗
3. Zhang · Acta Mater · 2008 · 56 · 545110.1016/j.actamat.2008.07.040 ↗
4. Zhilyaev · Prog Mater Sci · 2008 · 53 · 89310.1016/j.pmatsci.2008.03.002 ↗
5. Zhang · Acta Mater · 2010 · 58 · 169810.1016/j.actamat.2009.11.012 ↗
6. Hafok · Phil Mag · 2008 · 88 · 185710.1080/14786430802337071 ↗
7. Krasilnikov · Mater Sci Eng A · 2005 · 397 · 33010.1016/j.msea.2005.03.001 ↗
8. Neishi · Mater Sci Eng A · 2002 · 325 · 5410.1016/S0921-5093(01)01404-6 ↗
9. Schafler · Mater Sci Eng A · 2004 · 387–389 · 79910.1016/j.msea.2004.01.112 ↗
10. Zhilyaev · Scripta Mater · 2001 · 44 · 275310.1016/S1359-6462(01)00955-1 ↗
11. Zhilyaev · Mater Sci Eng A · 2008 · 489 · 20710.1016/j.msea.2007.12.031 ↗
12. Vorhauer · Scripta Mater · 2004 · 51 · 92110.1016/j.scriptamat.2004.04.025 ↗
13. Vorhauer · Metall Mater Trans A: Phys Metall Mater Sci · 2008 · 39 · 41710.1007/s11661-007-9413-1 ↗
14. Rathmayr GB, Pippan R. In: Nanomaterials by severe plastic deformation: NanoSPD5. Materials science forum. Stafa-Zuerich, Switzerland: Trans Tech Publications LTD; 2011. p. 797.
15. Tabor · Br J Appl Phys · 1956 · 7 · 15910.1088/0508-3443/7/5/301 ↗
16. Miller · 1996
17. Scheriau · J Magn Magn Mater · 2010 · 322 · 298410.1016/j.jmmm.2010.04.032 ↗
18. Bachmaier · Scripta Mater · 2009 · 61 · 101610.1016/j.scriptamat.2009.08.016 ↗
19. Yang · Saarbrücker Reihe Materialwissenschaft und Werkstofftechnik · 2006 · 8 · 132
20. Lücke · Acta Metall · 1971 · 19 · 108710.1016/0001-6160(71)90041-1 ↗
21. Cahn · Acta Metall · 1962 · 10 · 78910.1016/0001-6160(62)90092-5 ↗
22. Mendelev · Acta Mater · 2001 · 49 · 284310.1016/S1359-6454(01)00175-6 ↗
23. Xiao · Mater Sci Eng A · 2001 · 301 · 3510.1016/S0921-5093(00)01392-7 ↗