Microstructural evolution and its influence on creep and stress relaxation in nanocrystalline Ni

Abstract Indentation creep and stress relaxation tests were performed on rolled and annealed nanocrystalline (NC) Ni to study the influence of microstructure evolution on plastic deformation behavior. Dislocation density (ρ) increases with increasing rolling strain, reaching a maximum at 20% strain, followed by a decrease at larger strain. The ρ of Ni decreases significantly with increasing annealing temperature. Softening behavior is observed in NC Ni with grain size