Influence of the Si–O–C interplayer on the flexural behaviors of C/Si–C–N composites

Carbon fiber reinforced Si–C–N matrix composite(C/Si–C–N) with a Si–O–C interlayer (C/Si–O–C/Si–C–N) was fabricated via CVI and PIP process. The flexural behaviors of C/Si–O–C/Si–C–N were investigated using the three-point-bending method and the SEM technique. The results indicated that the flexural strengh of the C/Si–O–C/Si–C–N increases with increasing temperature and the modulus of the composite is essentially unchanged. The strength of C/Si–O–C/Si–C–N is comparable to that of C/PyC/Si–C–N, and the role of Si–O–C interlayer in C/Si–C–N can rival that of the PyC interlayer. The weaker interfacial bonding and the larger thickness of Si–O–C interlayer make a contribution to this at RT while the thinner interlayer and unstable structure of Si–O–C interphase do it above 1300 °C.