On the ω phase formation in Cr–Al and Ti–Al–Cr alloys

Abstract The interaction between Al and the transition metals Ti and Cr on the stability of the ω phase in metastable β-based structures was studied. Alloys were quenched from the melt to retain at room temperature a metastable β phase (B2 structure), which is stable at high temperatures. The structural study of the ω phase was carried out by correlating the deviation of ω structure from the ideal ω phase to the compositions of the parent β phase. Deviation of ω structures from the ideal one was related to the electron concentration of the parent β phase. A diffuse ω structure is reported in the Cr2Al phase (C11b structure) for the first time. The results are consistent with our previous suggestions that Al stabilises the ω phase in transition metals by lowering the spatial conduction electron concentration in the parent β phase and by enhancing p–d hybridisation of valence electrons. In the ternary Ti–Al–Cr alloys, prolonged annealing of the Ti–30Al–10Cr and Ti–20Al–10Cr alloys at 450°C led to the formation of two types of ordered crystalline ω structure.