Influence of silanized bacterial cellulose on the mode I interlaminar fracture toughness of glass fiber filled with epoxy resin
Source abstract
Abstract
In the present work, the bacterial cellulose was grafted with silane coupling agent and its characteristics were determined with help of Fourier-transform infrared spectroscopy, Nuclear magnetic resonance spectroscopy. The silanized bacterial cellulose was used as toughener for both epoxy resin and glass fiber reinforced epoxy resin composites. Both the epoxy bulk composites and glass fiber-filled epoxy composites were prepared via three steps hot curing processing using 4, 4ʹ – diamino diphenyl sulfone (DDS) as hardener and salicylic acid (HX) as an accelerator. The curing profile of epoxy with curing agent was also studied with help of differential scanning calorimetry (DDS). The tensile properties, fracture toughness, and morphology of both epoxy bulk composites and glass fiber composites were investigated in detail. The mechanism fracture toughness was also proposed to explain for the improvement of interlaminar fracture toughness of glass fiber-filled epoxy composite.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Epoxy Resin Curing Processes · Fiber-reinforced polymer composites · Mechanical Behavior of Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Faculty of Chemical - Physical Engineering, Le Qui Don Technical University, Bac Tu Liem, Hanoi, Vietnam
Faculty of Natural Sciences, Electric Power University, Hanoi, Vietnam
Funding
FOSTECT
References (50)
Show source-provided references
1. 10.1080/09276440.2020.172903110.1080/09276440.2020.1729031 ↗
2. 10.1007/s13233-020-8102-410.1007/s13233-020-8102-4 ↗
3. 10.1002/app.4827610.1002/app.48276 ↗
4. 10.1007/s13233-020-8010-710.1007/s13233-020-8010-7 ↗
5. 10.1038/s41428-019-0275-310.1038/s41428-019-0275-3 ↗
6. 10.1177/073490411990099010.1177/0734904119900990 ↗
7. 10.1134/S0965545X1603019610.1134/S0965545X16030196 ↗
8. 10.1007/s00289-018-2296-z10.1007/s00289-018-2296-z ↗
9. 10.1177/095400831984040410.1177/0954008319840404 ↗
10. 10.1007/s00289-018-2308-z10.1007/s00289-018-2308-z ↗
11. 10.7317/pk.2014.38.6.72610.7317/pk.2014.38.6.726 ↗
12. 10.1007/s00289-017-2162-410.1007/s00289-017-2162-4 ↗
13. 10.1007/s00289-015-1553-710.1007/s00289-015-1553-7 ↗
14. 10.1007/s10570-017-1503-710.1007/s10570-017-1503-7 ↗
15. 10.1016/j.polymertesting.2018.09.00510.1016/j.polymertesting.2018.09.005 ↗
16. 10.1016/j.compscitech.2020.10852310.1016/j.compscitech.2020.108523 ↗
17. 10.1016/j.compscitech.2020.10849310.1016/j.compscitech.2020.108493 ↗
18. 10.1016/j.compstruct.2020.11351010.1016/j.compstruct.2020.113510 ↗
19. 10.1080/03602559.2015.113245910.1080/03602559.2015.1132459 ↗
20. 10.1134/S0965545X1703002610.1134/S0965545X17030026 ↗
21. 10.1016/j.polymertesting.2017.05.01310.1016/j.polymertesting.2017.05.013 ↗
22. 10.1016/j.polymertesting.2019.10625610.1016/j.polymertesting.2019.106256 ↗
23. 10.1016/j.matpr.2018.06.60210.1016/j.matpr.2018.06.602 ↗
24. 10.1016/j.compositesa.2015.10.01710.1016/j.compositesa.2015.10.017 ↗
25. Tsai JL · Process Eng · 2011 · 14 · 1982
26. 10.1016/j.polymertesting.2019.01.01710.1016/j.polymertesting.2019.01.017 ↗
27. 10.1016/j.cej.2019.12232310.1016/j.cej.2019.122323 ↗
28. 10.1016/j.carbpol.2020.11736610.1016/j.carbpol.2020.117366 ↗
29. 10.1016/j.jmst.2015.08.01410.1016/j.jmst.2015.08.014 ↗
30. 10.1039/C9TA12536A10.1039/C9TA12536A ↗
31. 10.1016/j.carbon.2018.01.03510.1016/j.carbon.2018.01.035 ↗
32. 10.1039/C9TB02880C10.1039/C9TB02880C ↗
33. 10.1039/C8RA05536J10.1039/C8RA05536J ↗
34. 10.1016/j.carbpol.2020.11722810.1016/j.carbpol.2020.117228 ↗
35. 10.1039/C9NJ02199J10.1039/C9NJ02199J ↗
36. 10.1039/C4RA13057J10.1039/C4RA13057J ↗
37. 10.1039/C5TC02359A10.1039/C5TC02359A ↗
38. 10.1039/C9NR06028F10.1039/C9NR06028F ↗
39. 10.1039/D0NR03591B10.1039/D0NR03591B ↗
40. 10.1039/C1RA00719J10.1039/C1RA00719J ↗
41. 10.1039/C8RA03965H10.1039/C8RA03965H ↗
42. 10.1016/j.compositesb.2017.07.07010.1016/j.compositesb.2017.07.070 ↗
43. 10.1016/j.compositesa.2013.02.01110.1016/j.compositesa.2013.02.011 ↗
44. 10.3390/polym706102010.3390/polym7061020 ↗
45. 10.1016/j.engfracmech.2006.05.01510.1016/j.engfracmech.2006.05.015 ↗
46. 10.1163/15685540878381091110.1163/156855408783810911 ↗
47. 10.1016/0021-9797(84)90301-110.1016/0021-9797(84)90301-1 ↗
48. 10.1039/C6RA12356B10.1039/C6RA12356B ↗
49. 10.1016/j.carbpol.2016.05.10710.1016/j.carbpol.2016.05.107 ↗
50. 10.1039/C4RA09126D10.1039/C4RA09126D ↗