Ab initio study on plane defects in zirconium–hydrogen solid solution and zirconium hydride

Yutaka Udagawa, Masatake Yamaguchi, Hiroaki Abe, Naoto Sekimura, Toyoshi Fuketa

Acta Materialia· Volume 58· Issue 11
Publisher page

Abstract

Abstract Hydrogen embrittlement of zirconium alloys is one of the main causes of the mechanical degradation of the fuel cladding in light water reactors, and has therefore been extensively studied. Although various conjectures have been proposed as the origin of such embrittlement, it is not known which one plays the most important role: the brittle nature of the hydride, micro-crack nucleation by interaction of hydride precipitates with dislocations or void nucleation at the interface between hydride precipitates and zirconium matrix. The purpose of the present study was to elucidate the origin of the embrittlement by investigating the fracture properties of the hydride. We have evaluated the surface energy γ S and unstable stacking energy γ US of Zr–H systems by using ab initio calculations. The ductile/brittle behavior of the hydride is discussed based on the difference between γ S and γ US among the hydride, pure zirconium and hydrogen solid solution. For the solid solution at a H/Zr ratio less than 0.5 we obtained a monotonous decrease by 15–34% and 50–100% in γ S and γ US , respectively, from those in pure zirconium, indicating a reduction in both brittleness and ductility. Thus, hydrogen-induced embrittlement of the hcp Zr matrix was not confirmed. On the other hand, for the hydride we obtained a 25% smaller γ S and a 200–300% larger γ US than those in pure zirconium. This indicates that zirconium hydride has an extremely brittle nature due to the synergistic effect of a small γ S , implying easy generation of a fracture surface, and large γ US , implying a difficulty in dislocation motion, compared with pure zirconium. Furthermore, Rice’s ductile/brittle parameter D was 1.4 in the δ -hydride, indicating that it undergoes brittle fracture more easily than iridium, known as an extremely brittle material. These results seem sufficient to attribute hydrogen embrittlement of zirconium alloys substantially to the brittle nature of the hydride.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (38)

Show source-provided references
1. Fuketa · J Nucl Sci Technol · 2006 · 43 · 108010.1080/18811248.2006.9711198 ↗
2. Simpson · J Nucl Mater · 1979 · 87 · 30310.1016/0022-3115(79)90567-1 ↗
3. Kuroda · J Nucl Sci Technol · 2000 · 37 · 67010.1080/18811248.2000.9714942 ↗
4. Xu · J Nucl Mater · 2004 · 327 · 16510.1016/j.jnucmat.2004.02.004 ↗
5. Shi · J Nucl Mater · 1999 · 275 · 31210.1016/S0022-3115(99)00132-4 ↗
6. Puls · Metall Mater Trans A · 1991 · 22 · 232710.1007/BF02664999 ↗
7. Grange · Metall Mater Trans A · 2000 · 31 · 67910.1007/s11661-000-0010-9 ↗
8. Chan · Acta Metall Mater · 1995 · 43 · 432510.1016/0956-7151(95)00133-G ↗
9. Farrow · J Nucl Mater · 1965 · 15 · 20810.1016/0022-3115(65)90182-0 ↗
10. Kim · Nucl Eng Des · 2008 · 238 · 144110.1016/j.nucengdes.2007.10.020 ↗
11. Orowan · Rep Prog Phys · 1949 · 12 · 18510.1088/0034-4885/12/1/309 ↗
12. Rice · J Mech Phys Solids · 1992 · 40 · 23910.1016/S0022-5096(05)80012-2 ↗
13. Domain · Acta Mater · 2002 · 50 · 351310.1016/S1359-6454(02)00173-8 ↗
14. Domain · Acta Mater · 2004 · 52 · 149510.1016/j.actamat.2003.11.031 ↗
15. Kresse · Phys Rev B · 1993 · 47 · 55810.1103/PhysRevB.47.558 ↗
16. Kresse · Phys Rev B · 1996 · 54 · 1116910.1103/PhysRevB.54.11169 ↗
17. Kresse · Phys Rev B · 1999 · 59 · 175810.1103/PhysRevB.59.1758 ↗
18. Perdew · Phys Rev Lett · 1996 · 77 · 386510.1103/PhysRevLett.77.3865 ↗
19. Carpenter · Acta Metall · 1978 · 26 · 122510.1016/0001-6160(78)90006-8 ↗
20. Momma · J Appl Crystallogr · 2008 · 41 · 65310.1107/S0021889808012016 ↗
21. Duesbery · Acta Mater · 1998 · 46 · 148110.1016/S1359-6454(97)00367-4 ↗
22. Fukai · 1993
23. Patton · Phys Rev B · 1997 · 55 · 745410.1103/PhysRevB.55.7454 ↗
24. Jomard · Philos Mag Part B · 1998 · 77 · 6710.1080/13642819808206383 ↗
25. Zuzek · J Phase Equilib · 1990 · 11 · 385
26. Coughlin · J Am Chem Soc · 1950 · 72 · 226210.1021/ja01161a106 ↗
27. Fast · Phys Rev B · 1995 · 51 · 1743110.1103/PhysRevB.51.17431 ↗
28. Simmons · 1971
29. Nishizaki · Trans Atom Energy Soc Jpn · 2002 · 1 · 32810.3327/taesj2002.1.328 ↗
30. Surface Energies of Solid Metals
31. Legrand · Philos Mag B · 1984 · 49 · 17110.1080/13642818408227636 ↗
32. Akhtar · Acta Metall · 1971 · 19 · 65510.1016/0001-6160(71)90019-8 ↗
33. Yamaguchi · Phys Rev B · 2007 · 76 · 3541810.1103/PhysRevB.76.035418 ↗
34. Grigoriev · J Nucl Mater · 1998 · 257 · 9910.1016/S0022-3115(98)00445-0 ↗
35. Flanagan ME, Koss DA, Motta AT. The influence of hydrogen on the deformation behavior of zircaloy-4. In: Proceedings of the 2008 water reactor fuel performance meeting, Seoul, 2008.
36. Weatherly · Acta Metall · 1981 · 29 · 50110.1016/0001-6160(81)90074-2 ↗
37. Iwasawa M, Onuma T, Soneda N. Q04004, CRIEPI; 2005. Available from: http://criepi.denken.or.jp/jp/kenkikaku/cgi-bin/report_reference.cgi.
38. Shinohara · J Nucl Sci Technol · 2009 · 46 · 56410.1080/18811248.2007.9711563 ↗