Transition from nucleation controlled to growth controlled crystallization in Pd43Ni10Cu27P20 melts
Source abstract
Abstract
Abstract Crystallization of undercooled Pd 43 Ni 10 Cu 27 P 20 melts is studied in a differential scanning calorimeter. Isothermal experiments allow us for the first time to determine the entire crystallization kinetics of a metallic liquid as a function of time from the liquidus temperature to the glass transition temperature. The results are summarized in a time–temperature-transformation (TTT) diagram that reveals two time scales. One is given by the time to reach 1% of crystallized volume fraction and reflects the typical “nose” shape of the TTT-diagram. The other is the width of the crystallization event itself, which increases with decreasing temperature from 90 s at 793 K to 10,200 s at 623 K. Additional information about the crystallization process is gained by dividing the sample into about 300 particles that are processed simultaneously and crystallization of each individual particle can be detected. At high temperatures the onset of crystallization of individual particles are spread out over 1.5×10 5 s, whereas all particles crystallize simultaneously below the nose and the crystallization is not distinguishable from that of one large sample. The results suggest that the dominant crystallization mechanism changes in a very narrow temperature range from a nucleation-controlled process at high temperatures to a growth-controlled process at low temperatures.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallic Glasses and Amorphous Alloys · Material Dynamics and Properties · Mineralogy and Gemology Studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Kui · Appl. Phys. Lett. · 1984 · 45 · 61510.1063/1.95330 ↗
2. Inoue · Mater. Trans. JIM · 1990 · 31 · 10410.2320/matertrans1989.31.104 ↗
3. Inoue · Mater. Trans. JIM · 1990 · 31 · 17710.2320/matertrans1989.31.177 ↗
4. Peker · Appl. Phys. Lett. · 1993 · 63 · 234210.1063/1.110520 ↗
5. Nishiyama · Mater. Trans. JIM · 1996 · 37 · 153110.2320/matertrans1989.37.1531 ↗
6. Lu · J. Non-Cryst. Solids · 1999 · 250–252 · 57710.1016/S0022-3093(99)00135-0 ↗
7. Kim · Appl. Phys. Lett. · 1996 · 68 · 105710.1063/1.116247 ↗
8. Loeffler · Appl. Phys. Lett. · 2000 · 77 · 68110.1063/1.127084 ↗
9. Schroers · Appl. Phys. Lett. · 2000 · 77 · 115810.1063/1.1289033 ↗
10. Uhlmann · J. Non-Cryst. Solids · 1972 · 7 · 33710.1016/0022-3093(72)90269-4 ↗
11. Turnbull · J. Chem. Phys. · 1952 · 20 · 41110.1063/1.1700435 ↗
12. Perepezko · J. Non-Cryst. Solids · 1984 · 61–62 · 11310.1016/0022-3093(84)90538-6 ↗
13. Schroers · Appl. Phys. Lett. · 2000 · 76 · 234310.1063/1.126340 ↗
14. Avrami · J. Chem. Phys. · 1939 · 7 · 110310.1063/1.1750380 ↗
15. Nishiyama · Acta mater. · 1999 · 47 · 148710.1016/S1359-6454(99)00030-0 ↗
16. Turnbull · J. Appl. Phys. · 1950 · 21 · 102210.1063/1.1699435 ↗
17. Holland-Moritz · Acta mater. · 1998 · 5 · 160110.1016/S1359-6454(97)00341-8 ↗
18. Jackson · Trans. Metall. Soc. AIME · 1966 · 236 · 1129
19. Petarskaya, E., Schroers, J. and Johnson, W. L., MRS 2000 proceedings, in press.
20. Schroers · Int. J. Rap. Sol. · 1996 · 9 · 267
21. Busch · Appl. Phys. Lett. · 1995 · 67 · 154410.1063/1.114487 ↗
22. Borchers, C., Busch, R., Schroers, J. and Johnson, W. L., 2000, Acta mater., submitted for publication.10.1063/1.1289033 ↗
23. Kuno, M., Busch, R. and Schroers, J., 2001, Scripta mater., submitted for publication.
24. Bossuyt, S., 2001, Scripta mater., in press.
25. Drehman · Acta metal. · 1984 · 32 · 32310.1016/0001-6160(84)90105-6 ↗
26. Schneider · Appl. Phys. Lett. · 1996 · 68 · 49310.1063/1.116377 ↗
27. Wang · Appl. Phys. Lett. · 1997 · 71 · 105310.1063/1.119725 ↗
28. Schroers · Appl. Phys. Lett. · 1999 · 74 · 280610.1063/1.124020 ↗
29. Schroers · J. Appl. Phys. · 2000 · 88 · 4510.1063/1.373621 ↗
30. Granasy · J. Non-Cryst. Solids · 1993 · 162 · 30110.1016/0022-3093(93)91250-7 ↗