New strategy to improve the overall performance of single-crystal superalloys by designing a bimodal γ′ precipitation microstructure

Advanced single-crystal superalloys, developed to improve the high temperature capability of gas turbines, often underperform in low-temperature conditions. This limitation compromises the overall reliability of turbine blades under complex service environments. This study introduces a novel strategy to enhance the overall performance of a fourth-generation single-crystal superalloy. Rapid liquid-nitrogen quenching following the aging treatment promotes extensive nucleation of ultrafine γ′ particles (γ′ _γ ) with an average size of ∼10 nm, precipitated under extremely low supersaturation, as evidenced by high-resolution transmission electron microscopy (HRTEM) and atom probe tomography investigations. The combination of differential scanning calorimetry analysis, density functional theory calculations, and kinetic models verifies the high stability of γ′ _γ particles at low-temperature conditions around 900 °C. HRTEM observations reveal Orowan bypassing and dislocation cutting of γ′ _γ particles, leading to additional precipitation hardening by limiting dislocation motion in the γ phase and shear of primary precipitates. Consequently, a bimodal precipitation microstructure comprising γ′ _γ particles and primary γ′ phase significantly reduces the strain rate of low-temperature creep and nearly doubles the creep rupture life at 800 °C/735 MPa. Simultaneously, high-temperature properties at 900 °C/392 MPa and 1100 °C/137 MPa remain comparable to those of the original microstructure as the primary γ/γ′ microstructure is minimally affected by rapid cooling. This advancement improves overall performance and redefines the importance of small precipitates, broadening microstructure design concepts for future superalloy development.