Approaching the limits of dielectric breakdown for SiO2 films deposited by plasma-enhanced atomic layer deposition
Source abstract
Abstract
Abstract This study explores the ultimate limit in dielectric breakdown of SiO2 thin films deposited by gas-phase, plasma-enhanced atomic layer deposition. Thickness-dependent breakdown behaviors similar to conventional, thermally grown SiO2 thin films were observed for the first time on ALD films, where the dominant breakdown mechanisms were impact ionization, trap creation and anode hole injection, respectively. By suppressing these mechanisms, we show a reversible degradation in SiO2 after the onset of Fowler–Nordheim tunneling before permanent dielectric damage occurs. The reversible window was only observable in films thinner than 10 nm. The SiO2 thin films ultimately reached irreversible breakdown at a field strength of 2.7 V nm−1, where Si–O bonds were destroyed due to impact ionization and accelerated electrons.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Semiconductor materials and devices · Electronic and Structural Properties of Oxides · Copper Interconnects and Reliability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (37)
Show source-provided references
1. Choi · Mater Sci Eng R · 2011 · 72 · 9710.1016/j.mser.2010.12.001 ↗
2. Kingon · Nature · 2000 · 406 · 103210.1038/35023243 ↗
3. Wolf S, Tauber RN. Silicon processing for the VLSI Era, process technology, vol. 1, 2nd ed. Sunset Beach, CA: Lattice Press; 2000.
4. Bachmann · Angew Chem Int Ed · 2008 · 47 · 617710.1002/anie.200800245 ↗
5. Zhong · Chem Mater · 2004 · 16 · 109810.1021/cm0306111 ↗
6. Hiller · J Appl Phys · 2010 · 107 · 06431410.1063/1.3327430 ↗
7. Alexandrov · Chem Vap Deposition · 2005 · 11 · 48110.1002/cvde.200506385 ↗
8. O’Neill · Interface · 2011 · 20 · 33
9. Bravman · J Electr Microsc Tech · 1984 · 1 · 5310.1002/jemt.1060010106 ↗
10. Egerton · 2011
11. Alam · IEEE Trans Electron Devices · 2002 · 49 · 23210.1109/16.981212 ↗
12. DiMaria · J Appl Phys · 1993 · 73 · 336710.1063/1.352936 ↗
13. Abelein · Electron Device Lett IEEE · 2007 · 28 · 6510.1109/LED.2006.887629 ↗
14. DiMaria · Appl Phys Lett · 1992 · 61 · 232910.1063/1.108233 ↗
15. DiMaria · Appl Phys Lett · 1996 · 68 · 300410.1063/1.116678 ↗
16. Fang · IEEE Trans Electron Devices · 1994 · 41 · 103410.1109/16.293318 ↗
17. Tsu · Appl Phys Lett · 1973 · 22 · 56210.1063/1.1654509 ↗
18. Gehring · IEEE Trans Dev Mat Reliab · 2004 · 4 · 30610.1109/TDMR.2004.836727 ↗
19. Ashcroft · 1976
20. Nagano · J Appl Phys · 1994 · 75 · 353010.1063/1.356116 ↗
21. Salace · J Appl Phys · 1999 · 85 · 776810.1063/1.370583 ↗
22. Deal · J Phys Chem Solids · 1966 · 27 · 187310.1016/0022-3697(66)90118-1 ↗
23. Arnold · Phys Rev B · 1994 · 49 · 1027810.1103/PhysRevB.49.10278 ↗
24. Nozières · Phys Rev · 1958 · 109 · 74110.1103/PhysRev.109.741 ↗
25. Fischetti · Phys Rev B · 1985 · 31 · 209910.1103/PhysRevB.31.2099 ↗
26. DiStefano · J Vac Sci Technol · 1976 · 13 · 5010.1116/1.568911 ↗
27. Ozawa Y, Yamabe K. In: Extended abstracts of the 1991 international conference on solid state devices and materials. Jpn Soc Appl Phys; 1991. p. 240–2.
28. Kimoto · Appl Phys Lett · 2003 · 83 · 430610.1063/1.1629397 ↗
29. Roberts · J Phys D Appl Phys · 1981 · 14 · L1710.1088/0022-3727/14/3/001 ↗
30. Ragaie · Electron Lett · 1982 · 18 · 7410.1049/el:19820051 ↗
31. Tang · J Appl Phys · 1983 · 54 · 514510.1063/1.332738 ↗
32. Monsérié · Qual Reliab Eng Int · 1993 · 9 · 32110.1002/qre.4680090414 ↗
33. Klein · IEEE Trans Electron Devices · 1966 · 13 · 28110.1109/T-ED.1966.15681 ↗
34. Solomon · J Vac Sci Technol · 1977 · 14 · 112210.1116/1.569344 ↗
35. Batey · J Appl Phys · 1986 · 60 · 313610.1063/1.337726 ↗
36. Brydson · J Microsc · 1995 · 177 · 36910.1111/j.1365-2818.1995.tb03568.x ↗
37. Hansen · Microsc Microanal Microstr · 1994 · 5 · 17310.1051/mmm:0199400503017300 ↗