Study of pore closure during pressure-less sintering of advanced oxide ceramics
Source abstract
Abstract
Abstract Capsule-free hot isostatic pressing (HIP) represents a cost-effective variant to classical HIP allowing production of ceramics with top properties. For successful application of capsule-free HIP it is necessary to close all pores to prevent infiltration of the high-pressure gas into ceramics. This occurs when the sample completely transits from 2nd to 3rd stage of sintering, i.e. all open pores get closed at a density called critical density. A robust experimental study of this transition for several materials (alumina, magnesia-alumina spinel, tetragonal and cubic zirconia) has been carried out and compared with three theoretical models. From theoretical models it follows that critical density is a material parameter depending only on dihedral angle and being independent of particle size, green density and pore size distribution. It varies from 88.1% to 93.7% of theoretical density for studied materials and used models. Measured critical densities agree well with models by Beere and Carter & Glaeser for cubic systems (spinel and cubic zirconia). However, they do not match very well experimental data for alumina (hexagonal system) being in agreement with other open sources data. The sophisticated model by Svoboda et al. significantly underestimates the critical density for all systems. The reason of disagreement is analyzed in detail and several hypotheses explaining differences between the model and reality are proposed. It is recommended to use Beere’s and Carter’s & Glaeser’s models for prediction of critical density, while the model by Svoboda et al. characterizes rather the stage of pore closing initiation.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Powder Metallurgy Techniques and Materials · Aluminum Alloys Composites Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. Processing of nanocrystalline ceramics from ultrafine particles10.1179/imr.1996.41.3.85 ↗
2. Processing and properties of fine-grained transparent MgAl2O4 ceramics
3. Advanced spinel and sub-μm Al2O3 for transparent armour applications10.1016/j.jeurceramsoc.2008.03.024 ↗
4. Polycrystalline alumina ceramics doped with nanoparticles for increased transparency10.1016/j.jeurceramsoc.2014.09.041 ↗
5. Kang · 2005
6. Transparent alumina: a light-scattering model10.1111/j.1151-2916.2003.tb03325.x ↗
7. Effect of grain size on mechanical properties of 3Y-TZP ceramics
8. Theory of pore closure during sintering
9. Unifying theory of stability of penetrating liquid-phases and sintering pores10.1016/0001-6160(75)90078-4 ↗
10. The morphological stability of continuous intergranular phases: thermodynamic considerations10.1016/0001-6160(87)90231-8 ↗
11. Equilibrium pore surfaces, sintering stresses and constitutive-equations for the intermediate and late stages of sintering .1. Computation of equilibrium surfaces10.1016/0956-7151(94)90498-7 ↗
12. Sintering crystalline solids. I. Intermediate and final state diffusion models10.1063/1.1736107 ↗
13. On the instability of jets10.1112/plms/s1-10.1.4 ↗
14. Evaluated material properties for a sintered alpha-alumina10.1111/j.1151-2916.1997.tb03074.x ↗
15. Morrell · 1987
16. Magnesium aluminate (MgAl2O4) spinel produced via self-heat-sustained (SHS) technique10.1016/S0025-5408(01)00622-5 ↗
17. Hot-pressed MgAl2O4 for ultraviolet (uv), visible, and infrared (ir) optical requirements
18. Cubic-formation and grain-growth mechanisms in tetragonal zirconia polycrystal10.1111/j.1151-2916.2003.tb03483.x ↗
19. Properties of yttria stabilized tetragonal zirconia polycrystals
20. Sintering behavior of 0.8 mol%-CuO-Doped 3Y-TZP ceramics10.1111/j.1551-2916.2005.00679.x ↗
21. Effect of phase structure on sintering behavior of zirconia nanopowders10.1111/jace.12624 ↗
22. V. Pouchly, K. Maca, Sintering kinetic window for yttria-stabilized cubic zirconia, J. Eur. Ceram. Soc.. (n.d.). doi:10.1016/j.jeurceramsoc.2015.12.044.10.1016/j.jeurceramsoc.2015.12.044 ↗
23. Surface, grain-boundary and interfacial energies in Al2O3 and Al2O3-Sn, Al2O3-Co systems10.1007/BF00552390 ↗
24. Surface and grain-boundary energies in yttria-stabilized zirconia (YSZ-8 mol%)10.1007/BF01159310 ↗
25. Aspects of surface energy of ceramics
26. The sintering process10.1179/imr.1967.12.1.69 ↗
27. The sintering of open and closed porosity in UO210.1080/00318087508228691 ↗
28. Sintering of α-alumina for highly transparent ceramic applications10.1016/j.jeurceramsoc.2011.04.034 ↗
29. Transparent nanocrystalline bulk alumina obtained at 7.7 GPa and 800 °C10.1016/j.scriptamat.2013.05.017 ↗
30. Effect of particle size distribution on sintering of agglomerate-free submicron alumina powder compacts10.1016/S0955-2219(02)00009-2 ↗
31. Morphological changes in process-related large pores of granular compacted and sintered alumina10.1111/j.1151-2916.2000.tb01442.x ↗
32. Evolution of the grain size distribution during the sintering of alumina at 1350°C10.1111/j.1151-2916.2002.tb00387.x ↗
33. Transparent tetragonal yttria-stabilized zirconia ceramics: influence of scattering caused by birefringence10.1111/j.1551-2916.2010.04322.x ↗
34. Densification and grain growth of nanocrystalline 3Y-TZP during two-step sintering10.1016/j.jeurceramsoc.2008.04.030 ↗
35. Modeling densification during sinter-forging of yttria-partially-stabilized zirconia10.1016/0921-5093(95)09942-5 ↗
36. Mechanical properties and low-temperature aging of tetragonal zirconia polycrystals processed by hot isostatic pressing10.1557/JMR.2003.0337 ↗
37. Analysis of hot isotatic pressing of presintered zirconia10.1111/j.1151-2916.1990.tb05158.x ↗
38. From nanometric zirconia powder to transparent polycrystal10.1016/j.jeurceramsoc.2014.07.004 ↗
39. Transparent 8 mol% Y2O3–ZrO2 (8Y) ceramics10.1111/j.1551-2916.2007.02202.x ↗