Operando X-ray Studies of Crystalline Ge Anodes with Different Conductive Additives
Source abstract
Abstract
There is limited understanding of the lithiation reaction mechanisms for crystalline Ge and the effects of various battery components, including conductive additive type, on Ge transformations into amorphous and crystalline phases during electrochemical charge and discharge processes. In this work, we study the dependence of the phase transformations of crystalline Ge anodes on two common carbon-based conductive additives used in lithium-ion battery electrodes through operando X-ray diffraction and X-ray absorption spectroscopy. We find that Ge electrodes using carbon nanotubes as conductive additives exhibit higher structural and electrochemical reversibility compared with those with carbon black additives as well as better stability in cycling. On the basis of this, a proposed strategy to prolong the cycle life of crystalline Ge anodes is presented. Our operando XRD and XAS results show how the reaction pathways (phase transformations and local structural changes) of Ge anodes depend on conductive additive and impact the battery cycling performance.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Semiconductor materials and interfaces · Semiconductor materials and devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Science and Engineering, Stanford University, 496 Lomita Mall, Stanford, California 94305, United States
Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, 2575 Sand Hill Road, Menlo Park, California 94025, United States
School of Materials Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, Singapore 639798, Singapore
Funding
Energy Research Institute, Nanyang Technological University
References (29)
Show source-provided references
1. 10.1038/507026a10.1038/507026a ↗
2. 10.1039/b919877f10.1039/b919877f ↗
3. 10.1149/1.169741210.1149/1.1697412 ↗
4. 10.1021/nl403979s10.1021/nl403979s ↗
5. 10.1149/1.307387710.1149/1.3073877 ↗
6. 10.1103/PhysRev.96.2110.1103/PhysRev.96.21 ↗
7. 10.1021/ja047435x10.1021/ja047435x ↗
8. 10.1002/anie.20110306210.1002/anie.201103062 ↗
9. 10.1039/C4CC08722D10.1039/C4CC08722D ↗
10. 10.1039/c3ta13315j10.1039/c3ta13315j ↗
11. 10.1021/nl202411810.1021/nl2024118 ↗
12. 10.1149/1.283648110.1149/1.2836481 ↗
13. 10.1016/j.electacta.2010.06.08710.1016/j.electacta.2010.06.087 ↗
14. 10.1149/1.305598410.1149/1.3055984 ↗
15. 10.1021/cm501233k10.1021/cm501233k ↗
16. 10.1039/C4EE01384K10.1039/C4EE01384K ↗
17. 10.1021/la504382q10.1021/la504382q ↗
18. 10.1002/aenm.20150059910.1002/aenm.201500599 ↗
19. 10.1021/cm504312x10.1021/cm504312x ↗
20. 10.1002/adma.20090428510.1002/adma.200904285 ↗
21. 10.1039/b904116h10.1039/b904116h ↗
22. 10.1149/1.307431210.1149/1.3074312 ↗
23. 10.1016/j.elecom.2005.08.02410.1016/j.elecom.2005.08.024 ↗
24. 10.1016/j.electacta.2006.01.04310.1016/j.electacta.2006.01.043 ↗
25. 10.1039/C4TA02011A10.1039/C4TA02011A ↗
26. 10.1039/C4TA04350B10.1039/C4TA04350B ↗
27. 10.1021/ja511625910.1021/ja5116259 ↗
28. 10.1038/ncomms839310.1038/ncomms8393 ↗
29. 10.1021/nn900150y10.1021/nn900150y ↗