First-Principles Study of Lithiation of Type I Ba-Doped Silicon Clathrates
Source abstract
Abstract
Silicon clathrate materials, previously known for their superconducting and thermoelectric characteristics, have also recently been investigated for their electrochemical properties as anodes for lithium-ion batteries due to their unique cage structure and ability to incorporate extrinsic guest atoms. To better understand the preferred structures for small degrees of lithiation, first-principles density functional theory (DFT) was used to investigate the type I clathrate compounds Si 46, Li x Ba y Si 46 (0 ≤ x ≤ 8; y = 6, 8), and Li x Ba y Al 6 Si 40 (0 ≤ x ≤ 8; y = 6). The formation energies, electronic band structures, and density of states (DOS) were calculated. Lithium occupation in framework vacancies, empty and Ba-occupied cage cavities, and near the pentagonal and hexagonal faces of the clathrate polyhedra was considered. The data showed that Li insertion into framework or Ba vacancies could stabilize the clathrate structure. Silicon substitution by Al lowered the formation energies of the lithiated compounds and mitigated the calculated volume increase upon lithiation. The results also showed that it is energetically feasible for multiple guest atoms to be placed in the Si 24 cages. Changes in the clathrate atomic structure (e.g., bond lengths and angles) and electronic structure were highly dependent on the location of the Li and guest atom spacing within the clathrate framework. The results from this study can elucidate the preferred structural configurations for Li in type I, Ba-doped silicon clathrates and also be informative for efforts related to understanding the structures obtained after electrochemical insertion of lithium into silicon clathrates.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Battery Materials · Superconductivity in MgB2 and Alloys · Thermal Expansion and Ionic Conductivity
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
College of Letters and Sciences, Arizona State University, Mesa, Arizona 85212, United States
School of Physics and Optoelectronic Engineering, Xidian University, Xi’an 710071, People’s Republic of China
Materials Science and Engineering, School for Engineering of Matter, Transport and Energy, Arizona State University, Tempe, Arizona 85287, United States
Funding
Division of Materials Research
References (59)
Show source-provided references
1. 10.1126/science.150.3704.171310.1126/science.150.3704.1713 ↗
2. 10.1007/s10853-013-7973-610.1007/s10853-013-7973-6 ↗
3. 10.1021/ic020676q10.1021/ic020676q ↗
4. 10.1103/PhysRevB.66.01453210.1103/PhysRevB.66.014532 ↗
5. 10.1103/PhysRevLett.91.24700110.1103/PhysRevLett.91.247001 ↗
6. 10.1021/ic061241w10.1021/ic061241w ↗
7. 10.1016/j.jssc.2011.03.03810.1016/j.jssc.2011.03.038 ↗
8. 10.1021/ic102178d10.1021/ic102178d ↗
9. 10.1080/21663831.2013.86698810.1080/21663831.2013.866988 ↗
10. 10.1016/j.jssc.2004.01.01110.1016/j.jssc.2004.01.011 ↗
11. 10.1021/ja072470010.1021/ja0724700 ↗
12. 10.1021/ic900459210.1021/ic9004592 ↗
13. 10.1149/1.165242110.1149/1.1652421 ↗
14. 10.1149/1.173921710.1149/1.1739217 ↗
15. 10.1038/nnano.2007.41110.1038/nnano.2007.411 ↗
16. Miller, M. A.; Chan, K. S.; Liang, W.; Chan, C. K.Clathrate Allotropes for Rechargeable Batteries. U.S. Patent 8,906,551, 2014.
17. 10.1080/14786435.2014.99830810.1080/14786435.2014.998308 ↗
18. Nolas G. S. · 2014 · 19910.1007/978-94-017-9127-4 ↗
19. 10.1149/2.082208jes10.1149/2.082208jes ↗
20. 10.1002/celc.20130010410.1002/celc.201300104 ↗
21. 10.1039/c3ta11050h10.1039/c3ta11050h ↗
22. 10.1016/j.cplett.2005.04.07610.1016/j.cplett.2005.04.076 ↗
23. 10.1103/PhysRevB.64.04520610.1103/PhysRevB.64.045206 ↗
24. 10.1021/ic990778p10.1021/ic990778p ↗
25. 10.1021/ic200185910.1021/ic2001859 ↗
26. 10.1016/j.jpcs.2003.10.02510.1016/j.jpcs.2003.10.025 ↗
27. 10.1038/nmat98110.1038/nmat981 ↗
28. 10.1016/0022-5088(86)90609-010.1016/0022-5088(86)90609-0 ↗
29. 10.1021/ic202762610.1021/ic2027626 ↗
30. 10.1002/advs.20150005710.1002/advs.201500057 ↗
31. 10.1103/PhysRevB.59.175810.1103/PhysRevB.59.1758 ↗
32. 10.1103/PhysRevB.54.1116910.1103/PhysRevB.54.11169 ↗
33. 10.1103/PhysRevLett.77.386510.1103/PhysRevLett.77.3865 ↗
34. 10.1063/1.137094910.1063/1.1370949 ↗
35. 10.1088/0953-8984/20/41/41521410.1088/0953-8984/20/41/415214 ↗
36. 10.1016/j.jallcom.2013.10.19010.1016/j.jallcom.2013.10.190 ↗
37. 10.1103/PhysRevB.78.13410610.1103/PhysRevB.78.134106 ↗
38. 10.1016/j.scriptamat.2015.07.02110.1016/j.scriptamat.2015.07.021 ↗
39. 10.1002/jcc.2057510.1002/jcc.20575 ↗
40. 10.1149/1.183809910.1149/1.1838099 ↗
41. 10.1103/PhysRevB.56.135410.1103/PhysRevB.56.1354 ↗
42. 10.1103/PhysRevB.61.985910.1103/PhysRevB.61.9859 ↗
43. 10.1039/b801115j10.1039/b801115j ↗
44. 10.1021/ic202095e10.1021/ic202095e ↗
45. 10.1021/ic202481410.1021/ic2024814 ↗
46. 10.1002/chem.20120206910.1002/chem.201202069 ↗
47. 10.1006/jssc.2000.875510.1006/jssc.2000.8755 ↗
48. 10.1016/j.crci.2009.05.00410.1016/j.crci.2009.05.004 ↗
49. 10.1103/PhysRevLett.74.142710.1103/PhysRevLett.74.1427 ↗
50. 10.1021/ic062115v10.1021/ic062115v ↗
51. 10.1021/ja502733e10.1021/ja502733e ↗
52. 10.1063/1.480731610.1063/1.4807316 ↗
53. 10.1039/B916400F10.1039/B916400F ↗
54. 10.1103/PhysRevB.51.262810.1103/PhysRevB.51.2628 ↗
55. 10.1002/zaac.20040026810.1002/zaac.200400268 ↗
56. 10.1063/1.216986910.1063/1.2169869 ↗
57. 10.1006/jssc.2000.890610.1006/jssc.2000.8906 ↗
58. 10.1088/0953-8984/14/34/31810.1088/0953-8984/14/34/318 ↗
59. 10.1021/jacs.5b0788310.1021/jacs.5b07883 ↗