Improving the mechanical properties of Fe – TiB2 high modulus steels through controlled solidification processes

Abstract We investigated novel pathways to improve the mechanical properties of liquid metallurgy produced Fe – TiB 2 based high modulus steels (HMS) by controlled solidification kinetics and subsequent thermo-mechanical treatments. The solidification rate was varied by casting of hyper-eutectic alloys (20 vol% TiB 2 ) into moulds with differing internal thickness. Ingots between 5 and 40 mm thickness exhibited irregular particle microstructure consisting of sharp-edged coarse primary particles (increasingly clustered with slower solidification) and closely spaced irregular lamellae. Casting defects can be alleviated by hot rolling, but the mechanical properties remain unsatisfactory. Increasing the solidification rate results only at mould thicknesses of 4 mm and below in a significant refinement of the particle microstructure, necessitating liquid metal deposition techniques to utilise it for obtained improved mechanical performance of HMS. Decreasing the solidification rate causes density-induced floatation of the primary particles, which can be used in block-casting for the production of alloys consisting of small and spheroidised eutectic particles, exhibiting high ductility and superior toughness. Annealing just above the solidus-temperature allows the eutectic zones to liquefy and sink, leaving only primary TiB 2 particles behind in the top zone of the alloy. Despite the increased particle fraction up to 24 vol%, both strength, specific modulus and ductility are improved over standard processed HMS alloys with 20 vol% TiB 2 .