journal article·2011-06

Mechanisms of toughening in silicon nitrides: The roles of crack bridging and microstructure

S. Fünfschilling, T. Fett, M.J. Hoffmann, R. Oberacker, T. Schwind, J. Wippler, T. Böhlke, H. Özcoban, G.A. Schneider, P.F. Becher, J.J. Kruzic

Acta Materialia· Volume 59· Issue 10
Publisher page

Abstract

Crack-bridging mechanisms can provide substantial increases in toughness coupled with strength in ceramics. Herein, we describe the various bridging mechanisms, their toughening contributions and how they are affected by microstructure in silicon nitride ceramics, which are a classic example where both high strength and toughness are achieved. Crack growth resistance curves (R-curves) for seven different silicon nitrides doped with various metal oxides and with different microstructures were measured, and bridging stress distributions were calculated for each. Based on an analysis of those results combined with results of the relative interfacial toughness of two of the ceramics, a new mechanistic theory for the evolution of the R-curve is proposed. The initial steep rise in toughness is attributed to the formation of elastic bridges that experience no debonding. This mechanism has not previously been recognized in the literature and the high strength of these materials (up to 1 GPa) is here attributed primarily to that mechanism. As those bridges begin to fracture and the mechanism becomes saturated, a change in the R-curve slope is observed and the more traditional mechanisms of partially debonded elastic and fully debonded frictional bridges dominate the continuing rise in toughness. Furthermore, the saturation of each mechanism is associated with a change in slope of the R-curve. The results of this study provide a fundamental insight into how to optimize silicon nitride microstructures for high strength and toughness.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Metal and Thin Film Mechanics · MXene and MAX Phase Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (23)

Show source-provided references
1. Evans · J Am Ceram Soc · 1990 · 73 · 18710.1111/j.1151-2916.1990.tb06493.x ↗
2. Mai · J Am Ceram Soc · 1987 · 70 · 28910.1111/j.1151-2916.1987.tb04983.x ↗
3. Bennison · Acta Metall · 1989 · 37 · 265910.1016/0001-6160(89)90299-X ↗
4. Becher · J Am Ceram Soc · 1991 · 74 · 25510.1111/j.1151-2916.1991.tb06872.x ↗
5. Kovalev · J Am Ceram Soc · 2000 · 83 · 81710.1111/j.1151-2916.2000.tb01280.x ↗
6. Foulk · J Mech Phys Solids · 2007 · 55 · 71910.1016/j.jmps.2006.10.009 ↗
7. Kruzic · J Am Ceram Soc · 2008 · 91 · 198610.1111/j.1551-2916.2008.02380.x ↗
8. Fett · J Am Ceram Soc · 2008 · 91 · 363810.1111/j.1551-2916.2008.02750.x ↗
9. Fünfschilling · J Mater Sci · 2009 · 44 · 390010.1007/s10853-009-3507-7 ↗
10. Satet · J Am Ceram Soc · 2005 · 88 · 248510.1111/j.1551-2916.2005.00421.x ↗
11. Fünfschilling · J Am Ceram Soc · 2010 · 93 · 281410.1111/j.1551-2916.2010.03758.x ↗
12. Fünfschilling · J Mater Sci · 2008 · 44 · 33510.1007/s10853-008-3136-6 ↗
13. Fünfschilling S, Fett T, Oberacker R, Hoffmann MJ, Schneider GA, Becher PF, Kruzic JJ. J Am Ceram Soc, in press, DOI: 10.1111/j.1551-2916.2010.04329.x.10.1111/j.1551-2916.2010.04329.x ↗
14. Fett · J Am Ceram Soc · 1995 · 78 · 94910.1111/j.1151-2916.1995.tb08420.x ↗
15. Fett · Arch Appl Mech · 2006 · 76 · 66710.1007/s00419-006-0055-3 ↗
16. Fett · 1997
17. Fünfschilling · J Eur Ceram Soc · 2010 · 30 · 122910.1016/j.jeurceramsoc.2009.11.013 ↗
18. Becher · Mater Sci Eng · 2006 · A422 · 8510.1016/j.msea.2006.01.006 ↗
19. Becher · Acta Mater · 1996 · 44 · 388110.1016/S1359-6454(96)00069-9 ↗
20. Gao · J Appl Mech · 1989 · 56 · 82810.1115/1.3176178 ↗
21. Roux · Eur J Mech A/Solids · 2003 · 22 · 74310.1016/S0997-7538(03)00078-0 ↗
22. Lemercier · J Non-Cryst Sol · 1996 · 201 · 12810.1016/0022-3093(96)00147-0 ↗
23. Vogelgesang · Appl Phys Lett · 2000 · 76 · 98210.1063/1.125913 ↗