Abstract
Abstract Modelling and targeted experimentation are used to quantify the processing conditions which cause recrystallization in a single-crystal superalloy. The plasticity needed is traced to the differential thermal contractions of the metal and its ceramic mould during processing. For typical cooling rates, the plasticity causing recrystallization is induced above 1000 °C, thus over a temperature interval of approximately 300 °C after solidification is complete. The total accumulated plastic strain needed for recrystallization is estimated to be in the range of 2–3%. Modelling is used to rationalize the influence of mould thickness, stress concentration factor and geometry on the induced plasticity. Negligible plastic strains were predicted in a solid casting with no stress concentration features, as found experimentally. However, recrystallization occurred in thin-walled sections, particularly beneath shroud-like features due to the plasticity induced there. The model provides the foundation for a systems-based approach which enables recrystallization to be predicted and thus avoided in new designs of turbine blade aerofoil.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallurgy and Material Forming · High Temperature Alloys and Creep · Aluminum Alloy Microstructure Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (25)
Show source-provided references
1. Cox · Mater Sci Technol · 2003 · 19 · 44010.1179/026708303225010731 ↗
2. Xie · Scr Mater · 2008 · 59 · 85810.1016/j.scriptamat.2008.06.032 ↗
3. Eidel · Acta Mater · 2011 · 59 · 176110.1016/j.actamat.2010.11.042 ↗
4. Zaafarani · Acta Mater · 2008 · 56 · 3110.1016/j.actamat.2007.09.001 ↗
5. Zaafarani · Acta Mater · 2006 · 54 · 186310.1016/j.actamat.2005.12.014 ↗
6. Chen · Acta Mater · 2002 · 50 · 109510.1016/S1359-6454(01)00410-4 ↗
7. Meng · Mater Sci Eng A · 2010 · 527 · 611910.1016/j.msea.2010.04.071 ↗
8. Schaef · Acta Mater · 2012 · 60 · 242510.1016/j.actamat.2012.01.013 ↗
9. Schaef · Acta Mater · 2011 · 59 · 184910.1016/j.actamat.2010.11.051 ↗
10. Moverare · Acta Mater · 2009 · 57 · 226610.1016/j.actamat.2009.01.027 ↗
11. Zambaldi · Mater Sci Eng A · 2007 · 454–455 · 434
12. Goldschmidt D, Paul U, Sahm PR. In: Antolovich SD et al., editor. Proceedings of “Superalloys 1992” conference. Seven Springs (PA): TMS; 1992. p. 155–64.10.7449/1992/Superalloys_1992_155_164 ↗
13. Burgel R, Portella PD, Preuhs J. In: Pollock TM et al., editor. Proceedings of “Superalloys 2000” conference. Seven Springs (PA): TMS; 2000. p. 229–38.10.7449/2000/Superalloys_2000_229_238 ↗
14. Wang · Scr Mater · 2006 · 55 · 45710.1016/j.scriptamat.2006.05.013 ↗
15. Xie · Scr Mater · 2012 · 66 · 37810.1016/j.scriptamat.2011.11.037 ↗
16. Wang · Mater Sci Eng A · 2012 · 532 · 48710.1016/j.msea.2011.11.015 ↗
17. Reed · 2006
18. Siebörger · Mater Sci Eng A · 2001 · 298 · 2610.1016/S0921-5093(00)01318-6 ↗
19. Quested · Mater Sci Technol · 2009 · 25 · 15410.1179/174328408X361454 ↗
20. MacLachlan · Mater Sci Eng A · 2001 · 302 · 27510.1016/S0921-5093(00)01829-3 ↗
21. Nair · 1995
22. Pabst · Ceramics – Silikáty · 2004 · 48 · 165
23. Green · 1998
24. Milligan · Metall Trans A · 1987 · 18A · 8510.1007/BF02646225 ↗
25. Schubert · Z Metall · 2003 · 94 · 70510.3139/146.030705 ↗