On the role of zinc on the formation and growth of intermetallic phases during interdiffusion between steel and aluminium alloys

Abstract The effect of Zn – both within Al and as a coating on steel – on the intermetallic phase formation and growth was systematically studied in controlled experiments, simulating the interfacial reactions taking place in dissimilar solid/solid and solid/liquid joining procedures. Independent from the reaction temperature, the addition of 1.05 at.% Zn (2.5 wt.%) to Al had no effect on the reaction layers’ build-up with the η phase (Al 5 Fe 2 ) as the dominant component, but accelerated their parabolic growth up to a factor of 13. While Zn-coatings on steel were found to be beneficial for the regular and even formation of intermetallic reaction zones in solid/liquid joining procedures, their role in solid-state processes was found to be more complex and, if no countermeasures are taken, extremely detrimental to the joint properties. Possible reasons for the Zn-induced growth acceleration are discussed, as well as consequences for possible optimisation steps for reducing harmful effects of Zn in dissimilar joints between Al alloys and steel.