The importance of sign and magnitude of γ/γ′ lattice misfit in superalloys—with special reference to the new γ′-hardened cobalt-base superalloys
Source abstract
Abstract
Abstract In this work, the remarkable high-temperature strength properties of monocrystalline γ′-hardened Ni-base superalloys are reviewed with the goal of understanding better the important role played by the γ/γ′ lattice misfit δ with respect to microstructural stability and high-temperature creep and fatigue resistance. In particular, attention is focussed on the phenomenon of microstructural degradation by directional coarsening in the form of γ/γ′ rafting which also occurs in turbine blades in service. The role played by the lattice misfit (which is negative for all currently used Ni-base superalloys) is elucidated with respect to its sign, magnitude and temperature dependence. Based on a detailed discussion of high-temperature deformation involving γ/γ′ rafting, it is argued that superalloys with a positive γ/γ′ lattice misfit should exhibit better high-temperature strength properties than otherwise similar superalloys with a negative misfit. In this context, the new class of γ′-hardened Co-base superalloys is of special interest. These alloys have promising high-temperature strength properties and possess a positive lattice mismatch. It is suggested that this positive mismatch is one of the beneficial factors that contribute to the promising properties of these alloys and that this aspect should be explored further.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: High Temperature Alloys and Creep · Advanced Materials Characterization Techniques · Intermetallics and Advanced Alloy Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (54)
Show source-provided references
1. Strudel · 1996 · 2105
2. Pollock · 2002 · vol. 11 · 547
3. Mughrabi · Adv Eng Mater · 2000 · 2 · 31910.1002/1527-2648(200006)2:6<319::AID-ADEM319>3.0.CO;2-S ↗
4. Reed · 2006
5. 2012
6. Nabarro · Metall Mater Trans A · 1996 · 27A · 51310.1007/BF02648942 ↗
7. Mughrabi · 1996 · 267
8. Mughrabi · Mater Sci Technol · 2009 · 25 · 19110.1179/174328408X361436 ↗
9. Pollock · Acta Metall · 1994 · 42 · 185910.1016/0956-7151(94)90011-6 ↗
10. Véron · Acta Metall Mater · 1996 · 44 · 363310.1016/1359-6454(96)00011-0 ↗
11. Feller-Kniepmeier · Metall Trans A · 1989 · 20 · 123310.1007/BF02647405 ↗
12. Buffière · Acta Metall Mater · 1995 · 43 · 179110.1016/0956-7151(94)00432-H ↗
13. Kamaraj · Mater Sci Eng A · 2001 · 319–321 · 79610.1016/S0921-5093(01)00950-9 ↗
14. Ott · Mater Sci Eng A · 1999 · 272 · 2410.1016/S0921-5093(99)00453-0 ↗
15. Draper · Metall Trans · 1989 · 20A · 68310.1007/BF02667585 ↗
16. von Grossmann · Philos Mag A · 2000 · 80 · 174310.1080/01418610008219081 ↗
17. Nathal · Mater Sci Eng A · 1985 · 75 · 19510.1016/0025-5416(85)90189-2 ↗
18. Biermann · Metall Trans · 1996 · 27A · 100310.1007/BF02649768 ↗
19. Zhang · Acta Mater · 2005 · 53 · 462310.1016/j.actamat.2005.06.013 ↗
20. Carroll · Metall Mater Trans A · 2008 · 39 · 129010.1007/s11661-008-9520-7 ↗
21. Rowland · 2004 · 697
22. Tetzlaff · 2000 · 273
23. Sato · Science · 2006 · 312 · 9010.1126/science.1121738 ↗
24. Suzuki · Scr Mater · 2007 · 56 · 38510.1016/j.scriptamat.2006.10.039 ↗
25. Pollock · JOM · 2010 · 62 · 5810.1007/s11837-010-0013-y ↗
26. Shinagawa · Scr Mater · 2009 · 6 · 61210.1016/j.scriptamat.2009.05.037 ↗
27. Bauer · 2012 · 695
28. Titus · 2012 · 823
29. Pyczak · Mater Sci Eng A · 2013 · 571 · 1310.1016/j.msea.2013.02.007 ↗
30. Tanaka · Philos Mag · 2012 · 92 · 401110.1080/14786435.2012.700416 ↗
31. Mughrabi H. Presented at First International Workshop on Advanced Cobalt-Based Superalloys, Pommersfelden, 2013, and private communication.
32. Pineau · Acta Metall · 1976 · 24 · 55910.1016/0001-6160(76)90101-2 ↗
33. Fredholm · 1984 · 211
34. Carry · Acta Metall · 1977 · 25 · 6710.1016/0001-6160(77)90092-X ↗
35. Fredholm · 1987 · 9
36. Mughrabi · 1996 · 115
37. Mughrabi · 1994 · 705
38. Schneider · 1993 · 209
39. Schneider W. [Doctoral Thesis]. Hochtemperaturkriechverhalten und Mikrostruktur der einkristallinen Nickelbasis-Superlegierung CMSX-4 bei Temperaturen von 800 C bis 1100 C, Universität Erlangen-Nürnberg, 1993.
40. Kraft · 1996 · 27
41. Blum · 1993 · 359
42. Hammer J, Mughrabi H. In: Exner HE, Schumacher V, editors. Proceedings of the First European Conference on Advanced Materials and Processes (EUROMAT ’89). Driver D, Mughrabi H, co-editors, Vol. 1: Advanced Processing and High Temperature Materials. DGM Informationsgesellschaft Verlag. 1989, pp. 445-450.
43. Hammer J. [Doctoral Thesis]: Kriech- und Zeitstandverhalten der einkristallinen Nickelbasis-Superlegierung SRR 99 unter besonderer Berücksichtigung der mikrostrukturellen Vorgänge und der Materialfehler, Universität Erlangen-Nürnberg; 1990.
44. Reed · Acta Mater · 1999 · 47 · 336710.1016/S1359-6454(99)00217-7 ↗
45. Tan · Mater Sci Eng A · 2013 · 580 · 2110.1016/j.msea.2013.05.028 ↗
46. Svoboda · Acta Mater · 1998 · 46 · 342110.1016/S1359-6454(98)00043-3 ↗
47. Shui · Mater Sci Eng A · 2006 · 418 · 22910.1016/j.msea.2005.11.028 ↗
48. Shui · Mater Sci Eng A · 2007 · 454–455 · 46110.1016/j.msea.2006.11.136 ↗
49. Tetzlaff U. [Doctoral Thesis] Gezielte gerichtete Vergröberung (Floßbildung) des γ/γ′-Gefüges und Auswirkungen auf die mechanischen Hochtemperatureigenschaften einer einkristallinen Nickelbasis-Superlegierung, Universität Erlangen-Nürnberg; 2000.
50. Müller · Acta Metall Mater · 1993 · 41 · 340110.1016/0956-7151(93)90220-M ↗
51. Svoboda J, Schweizer Ch, private communication, 2013.
52. Gao S, Ma A, Hartmeier A, presented at First International Workshop on Advanced Cobalt-Based Superalloys, Pommersfelden 2013, and private communication.
53. Biermann H. [Habilitation Thesis]: Ursachen und Auswirkungen der gerichteten Vergröberung (“Floßbildung”) in einkristallinen Nickelbasis-Superlegierungen, Universität Erlangen-Nürnberg; 1998.
54. Neumeier S, private communication, 2014.