High cooling rates and metastable phases at the interfaces of explosively welded materials
Source abstract
Abstract
Abstract During an explosion, the interfaces of welded materials experience fast heating due to high strain rate severe plastic deformation. This leads to the formation of local zones, where melting and mixing of welded materials is observed. These zones are frequently referred to as vortexes, eddies or swirls, due to the specific rotational movement of materials during mixing. This study is primarily devoted to the discussion of the structures that appear in these zones. Simple approaches to estimate the heating and cooling rates at the interfaces between explosively welded materials were proposed. It was concluded that the heating rate at the interfaces was of the order of 10 9 K/s, while the cooling rate achieved 10 7 K/s. Several combinations of explosively welded alloys (steel/steel, Ti alloy/steel, Zr/Cu, Zr/Ni, Ta/Cu, Al/magnesium alloy and Cu/brass) were thoroughly analyzed using scanning electron microscopy, transmission electron microscopy and energy dispersive X-ray spectroscopy. In most of these combinations, metastable crystalline, quasicrystalline or glassy phases were observed. The formation of different types of metastable phases is discussed with respect to the compositions of the welded alloys. It was concluded that solidification conditions at the interfaces of explosively welded materials are similar to those during rapid solidification. Thus, the results of numerous experiments on rapid solidification of alloys could be applied to analyze the structures that appear in mixing zones.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallic Glasses and Amorphous Alloys · Intermetallics and Advanced Alloy Properties · Quasicrystal Structures and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (53)
Show source-provided references
1. Zakharenko · 1990
2. Fundamentals, of explosive welding10.1080/00107516808204394 ↗
3. Crossland · 1982
4. Deribas · 1980
5. Formation of nonequilibrium phases at collision interface in an explosively welded Ti/Ni clad10.2320/matertrans1989.36.1338 ↗
6. Microstructure changes and phase growth occurring at the interface of the Al/Ti explosively welded and annealed joints10.1007/s11665-016-1978-7 ↗
7. P. Bazarnik, M. Cantoni, L. Śnieżek, M. Lewandowska, Characterization of the microstructure of composite Ti6Al4V-AA2519 obtained by explosive welding, European Microscopy Congress 2016: Proceedings, Wiley Online Library.
8. Hierarchical microstructure of explosive joints: example of titanium to steel cladding10.1016/j.msea.2010.11.092 ↗
9. Electron microscopy studies of bonding interface in explosively welded Ti/steel clads10.2355/isijinternational.35.217 ↗
10. A. Chiba, M. Nishida, Y. Morizono, Microstructure of bonding interface in explosively-welded clads and bonding mechanism, in: S. Itoh, K. Hokamoto, M. Fujita (Eds.) 1st International Symposium on Explosion, Shock Wave and Hypervelocity Phenomena (ESHP Symposium), Kumamoto, 2004, pp. 465–474.10.4028/www.scientific.net/MSF.465-466.465 ↗
11. Interfacial characterization and mechanical property of Ti/Cu clad sheet produced by explosive welding and annealing10.1007/s11595-015-1295-2 ↗
12. Characterization of explosive weld joints by TEM and SEM/EBSD10.2478/amm-2014-0197 ↗
13. Metallic glass formation at the interface of explosively welded Nb and stainless steel10.1007/s12540-015-5020-7 ↗
14. Explosively welded multilayer Ni-Al composites10.1016/j.matdes.2015.09.103 ↗
15. A new method for explosive welding of Al/ZrO2 joint using regulated underwater shock wave10.1016/S0924-0136(98)00286-6 ↗
16. Underwater explosive welding of thin tungsten foils and copper10.1016/j.jnucmat.2011.07.013 ↗
17. Numerical and experimental studies of the mechanism of the wavy interface formations in explosive/impact welding10.1016/j.jmps.2005.06.001 ↗
18. Metallic glass coating on metals plate by adjusted explosive welding technique10.1016/j.apsusc.2009.07.033 ↗
19. Popov · 1961
20. Formation and structure of vortex zones arising upon explosion welding of carbon steels10.1134/S0031918X12030039 ↗
21. D. Frey, J. Banker, Recent successes in tantalum clad pressure vessel manufacture: a new generation of tantalum clad vessel, Corrosion Solutions Conference, USA, 2003, pp. 163–169.
22. The Cu-Ta (Copper-Tantalum) system10.1007/BF02877637 ↗
23. Interaction at the contact interface between copper and zirconium, welded explosively10.1007/BF01463989 ↗
24. Bulk metallic glass formation in the binary Cu–Zr system10.1063/1.1751219 ↗
25. Glass formation in Ni-Zr-(Al) alloy systems
26. Analysis of explosively welded aluminum–AZ31 magnesium alloy joints10.2320/matertrans.MC200796 ↗
27. Thermodynamic description of the Al-Mg-Si system using a new formulation for the temperature dependence of the excess Gibbs energy10.1016/j.tca.2011.10.017 ↗
28. New metastable phases in the Al-Mg system10.1007/BF01729012 ↗
29. A near icosahedral quasiperiodic phase in rapidly solidified Mg32Al4910.1080/09500839108214685 ↗
30. From modulated phases to a quasiperiodic structure with a cubic point group and inflation symmetry
31. Cubic superspace symmetry and inflation rules in metastable MgAl alloy10.1007/s100510050591 ↗
32. A new icosahedral quasicrystal in rapidly solidified FeTi210.1016/0036-9748(86)90194-8 ↗
33. The microstructure of rapidly solidified Ti-Fe melt-spun ribbons10.1007/BF02670176 ↗
34. Microstructure of a rapidly solidified Ti73Fe27 melt-spun ribbon
35. The microstructure of rapidly solidified Ti-32wt% Fe melt-spun ribbon10.1007/BF00585474 ↗
36. Ni- and Cu-free Ti-based metallic glasses with potential biomedical application10.1016/j.intermet.2015.04.004 ↗
37. Dissipative structures during explosive welding
38. Thermal effects in the weld zone in explosive welding10.1007/BF00742828 ↗
39. Quantitative evaluation of critical cooling rate for metallic glasses10.1016/S0921-5093(00)01446-5 ↗
40. Estimation of critical cooling rates for glass formation in bulk metallic glasses through non-isothermal thermal analysis10.1007/BF03027478 ↗
41. Explosive cladding and post-weld heat treatment of mild steel and titanium10.1016/j.matdes.2015.12.120 ↗
42. Linear friction welding of Al-Cu part 2-Interfacial characteristics10.1179/000844311X13112418194671 ↗
43. Mechanical and microstructural characteristics of Ti6Al4V/AA2519 and Ti6Al4V/AA1050/AA2519 laminates manufactured by explosive welding10.1016/j.matdes.2016.08.088 ↗
44. Non-crystalline structure in solidified gold-silicon alloys10.1038/187869b0 ↗
45. Stabilization of metallic supercooled liquid and bulk amorphous alloys10.1016/S1359-6454(99)00300-6 ↗
46. Explosive welding: mixing of metals without mutual solubility (iron-silver)10.1134/S0031918X12110075 ↗
47. Lalena · 2010
48. Superior room-temperature ductility of typically brittle quasicrystals at small sizes10.1038/ncomms12261 ↗
49. Steinhardt · 1987
50. Shear band melting and serrated flow in metallic glasses10.1063/1.2956666 ↗
51. Local microstructure evolution at shear bands in metallic glasses with nanoscale phase separation
52. Experimental and physical model of the melting zone in the interface of the explosive cladding bar10.1016/j.jmrt.2016.04.001 ↗
53. Erratum: molecular dynamics study of the binary Cu46 Zr54 metallic glass motivated by experiments: glass formation and atomic-level structure (Physical Review B (2005) 71, (224208))10.1103/PhysRevB.74.019901 ↗