journal article·2005-11

Whisker and Hillock formation on Sn, Sn–Cu and Sn–Pb electrodeposits

W.J. Boettinger, C.E. Johnson, L.A. Bendersky, K.-W. Moon, M.E. Williams, G.R. Stafford

Acta Materialia· Volume 53· Issue 19
Publisher page

Abstract

High purity bright Sn, Sn–Cu and Sn–Pb layers, 3, 7 and 16 lm thick were electrodeposited on phosphor bronze cantilever beams in a rotating disk apparatus. Beam deflection measurements within 15 min of plating proved that all electrodeposits had in-plane compressive stress. In several days, the surfaces of the Sn–Cu deposits, which have the highest compressive stress, develop 50 lm contorted hillocks and 200 lm whiskers, pure Sn deposits develop 20 lm compact conical hillocks, and Sn–Pb deposits, which have the lowest compressive stress, remain unchanged. The differences between the initial compressive stresses for each alloy and pure Sn is due to the rapid precipitation of Cu6Sn5 or Pb particles, respectively, within supersaturated Sn grains produced by electrodeposition. Over longer time, analysis of beam deflection measurements indicates that the compressive stress is augmented by the formation of Cu6Sn5 on the bronze/Sn interface, while creep of the electrodeposit tends to decrease the compressive stress. Uniform creep occurs for Sn–Pb because it has an equi-axed grain structure. Localized creep in the form of hillocks and whiskers occurs for Sn and Sn–Cu because both have columnar structures. Compact hillocks form for the Sn deposits because the columnar grain boundaries are mobile. Contorted hillocks and whiskers form for the Sn–Cu deposits because the columnar grain boundary motion is impeded. Published by Elsevier Ltd on behalf of Acta Materialia Inc.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Electronic Packaging and Soldering Technologies · Advanced Welding Techniques Analysis · Aluminum Alloy Microstructure Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (43)

Show source-provided references
1. Furuta · Jpn J Appl Phys · 1969 · 8 · 140410.1143/JJAP.8.1404 ↗
2. Chason E, Kabakian L, Kumar S. Materials for space applications. In: Chipara M, Edwards DL, Benson RS, Phillips S, editors. Mater Res Soc Symp Proc, vol. 851, Warrendale, PA; 2005. p. NN5.17.
3. Fisher · Acta Metall · 1954 · 2 · 36810.1016/0001-6160(54)90053-X ↗
4. Arnold · Plating · 1966 · 53 · 96
5. Galyon GT. Annotated Tin Whisker Bibliography, National Electronics Manufacturing Initiative Inc. (NEMI), Herdon, VA, July; 2003. Available from: www.nemi.org.
6. Chadhari · J Appl Phys · 1974 · 45 · 433910.1063/1.1663054 ↗
7. Jackson · Acta Metall · 1982 · 30 · 199310.1016/0001-6160(82)90103-1 ↗
8. Doerner · CRC Crit Rev Solid State Mater Sci · 1988 · 14 · 22510.1080/10408438808243734 ↗
9. Tu · Acta Metall · 1973 · 21 · 34710.1016/0001-6160(73)90190-9 ↗
10. Tu · Phys Rev B-Cond Matter · 1994 · 49 · 203010.1103/PhysRevB.49.2030 ↗
11. Lee · Acta Mater · 1998 · 46 · 370110.1016/S1359-6454(98)00045-7 ↗
12. Moon · 2001 · 1115
13. Weil · Plating · 1971 · 58 · 137
14. Onishi · Trans J Inst Metal · 1975 · 16 · 53910.2320/matertrans1960.16.539 ↗
15. Tu · Acta Metall · 1982 · 30 · 94710.1016/0001-6160(82)90201-2 ↗
16. Stafford GR, Bertocci U, Guyer JE, NIST; 2004 [unpublished research].
17. Bard · 1980
18. Galyon GT, Palmer M, IBM; 2004, unpublished images of NIST samples.
19. Petersson · J Electroanal Chem · 2000 · 485 · 16610.1016/S0022-0728(00)00113-3 ↗
20. Tindall · Anal Chem · 1968 · 40 · 140210.1021/ac60266a017 ↗
21. Brenner · 1963 · vol. 1
22. Sheng · J Appl Phys · 2002 · 92 · 6410.1063/1.1481202 ↗
23. Kane · Acta Metall · 1966 · 14 · 60510.1016/0001-6160(66)90068-X ↗
24. Kim · J Mater Res · 2000 · 15 · 170910.1557/JMR.2000.0246 ↗
25. Brenner · J Res NBS · 1949 · 42 · 105
26. Smithells · 1967
27. Fields · 1992 · 165
28. Saunders · Bull Alloy Phase Diagram · 1990 · 11 · 27810.1007/BF03029299 ↗
29. Homer · J Inst Metal · 1939 · 64 · 169
30. Kattner UR. NIST, Gaithersburg, MD; 2002 [unpublished research].
31. Dyson · J Appl Phys · 1967 · 38 · 340810.1063/1.1710127 ↗
32. Warburton · Thin Solid Films · 1975 · 25 · 7110.1016/0040-6090(75)90247-3 ↗
33. Karakaya · Bull Alloy Phase Diagram · 1988 · 9 · 14410.1007/BF02890552 ↗
34. Lee · Proc Phys Soc · 1954 · 67 · 73710.1088/0370-1301/67/10/301 ↗
35. Yeh · Phys Rev Lett · 1984 · 53 · 146910.1103/PhysRevLett.53.1469 ↗
36. Floro · MRS Bull · 2002 · 27 · 1910.1557/mrs2002.15 ↗
37. Schneibel · J Mater Sci · 1983 · 18 · 56210.1007/BF00560645 ↗
38. McCabe · Metall Mater Trans · 2002 · 33A · 153110.1007/s11661-002-0075-8 ↗
39. Hutchinson · Mater Sci Forum · 2004 · 467–470 · 46510.4028/www.scientific.net/MSF.467-470.465 ↗
40. Kaur · 1989 · vol. 2
41. Coble · J Appl Phys · 1963 · 34 · 167910.1063/1.1702656 ↗
42. Raj · Metall Trans · 1971 · 2 · 111310.1007/BF02664244 ↗
43. Genin · J Appl Phys · 1995 · 77 · 513010.1063/1.359324 ↗