Thermally and plastically induced residual strains in textured Zircaloy-2 plate

The residual intergranular strains in textured Zircaloy-2 plate samples induced by cooling from 823 K to ambient temperatures, by cold-rolling by 1.5% and 25% and by deforming in tension by 1.5% were measured by neutron diffraction. The strong rolling texture, which gives rise to two ideal orientations, permitted the interpretation of much of the data in terms of strain tensors for the two orientations. The experimental results were compared with calculations based on the elasto-plastic self-consistent model with no adjustable parameters. Close agreement was obtained for samples in the as-cooled state and deformation in tension by 1.5% but the agreement is less satisfactory for cold-rolling.