Characterisation of the fracture properties in the ductile to brittle transition region of the weld material of a reactor pressure vessel
Source abstract
Abstract
This work presents the results of the fracture characterisation of the weld material of a nuclear vessel, currently in service, in the ductile to brittle transition region. The tests consisted of Charpy impact and tensile tests, performed in the framework of the surveillance programme of the plant. Moreover, in the context of this research, KJc fracture toughness tests on pre-cracked Charpy V notch specimens (evaluated according to the Master Curve methodology) together with some mini-tensile tests, were performed; non-irradiated and several irradiated material conditions were characterised. The analysis of the experimental results revealed some inconsistencies concerning the material embrittlement as measured through Charpy and KJc fracture tests: in order to obtain an adequate understanding of the results, an extended experimental scope well beyond the regulatory framework was developed, including Charpy tests and KJc fracture tests, both performed on reconstituted specimens. Moreover, Charpy specimens irradiated in the high flux BR2 material test reactor were tested with the same purpose. With this extensive experimental programme, a coherent and comprehensive description of the irradiation behaviour of the weld material in the transition region was achieved. Furthermore it revealed better material properties in comparison with the initial expectations based on the information obtained in the framework of the surveillance programme.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fatigue and fracture mechanics · Nuclear Materials and Properties · Nuclear and radioactivity studies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (33)
Show source-provided references
1. ASTM Standard E 399-90 (Reapproved 1997), Standard test method for plane-strain fracture toughness testing of metallic materials, Annual Book of ASTM Standards, vol. 03.01, ASTM International, West Conshohocken, PA, 2005.
2. Ferreño · Eng. Fract. Mech. · 2009 · 76 · 249510.1016/j.engfracmech.2009.08.010 ↗
3. Rules and Regulations Title 10. Code of federal regulations part 50.61, Appendix G, Fracture Toughness Requirements for Protection Against Pressurized Thermal Shock Events, Washington, DC, US Government Printing Office, US Nuclear Regulatory Commission (1986).
4. ASME Boiler and Pressure Vessel Code, Section XI, Inservice inspection of nuclear power plant, American Society for Mechanical Engineers, 2007.
5. ASME Boiler and Pressure Vessel Code, Section III, Rules for construction of nuclear power plant components, American Society of Mechanical Engineers, New York, 2007.
6. Regulatory Guide 1.99 Revision 2, Radiation embrittlement of reactor vessel materials, Office of Nuclear Regulatory Research, US Nuclear Regulatory Commission, Washington, DC, 1988.
7. Lucon · Int. J. Press. Vessels Pip. · 2007 · 84 · 53610.1016/j.ijpvp.2007.05.001 ↗
8. Wallin · Met. Sci. · 1984 · 18 · 1310.1179/030634584790420384 ↗
9. Wallin · Eng. Fract. Mech. · 1984 · 19 · 108510.1016/0013-7944(84)90153-X ↗
10. Wallin · Eng. Fract. Mech. · 1985 · 22 · 14910.1016/0013-7944(85)90167-5 ↗
11. K. Wallin, A simple theoretical Charpy V–KIc correlation for irradiation embrittlement, Innovative approaches to irradiation damage and fracture analysis, PVP 170, ASME, 1989, p. 93.
12. Valiente · Eng. Fract. Mech. · 2005 · 72 · 70910.1016/j.engfracmech.2004.06.004 ↗
13. ASTM Standard E1921-09-a, Standard Test Method for Determination of Reference Temperature, T0, for Ferritic Steels in the Transition Range, ASTM International, West Conshohocken, PA, 2008.
14. J.G. Merkle, K. Wallin, D.E. McCabe, Technical Basis for an ASTM Standard on Determining the Reference Temperature T0 for Ferritic Steel in the Transition Range, NUREG/CR-5504, USMNRC, 1998.
15. D. Ferreño, Integridad estructural de vasijas nucleares en base a la curva patrón obtenida mediante probetas reconstruidas, PhD thesis, University of Cantabria, Spain, 2008.
16. ASME Boiler and Pressure Vessel Code–Code Case N-629, Use of fracture toughness test data to establish reference temperature for pressure retaining materials, Section XI, Division 1, 1999.
17. ASME Boiler and Pressure Vessel Code–Code Case N-631, Use of fracture toughness test data to establish reference temperature for pressure retaining materials other than bolting for class 1 vessels, Section III, Division 1, 1999.
18. ASTM Standard E185-02, Standard Practice for Design of Surveillance Programs for Light-Water Moderated Nuclear Power Reactor Vessels, Annual Book of ASTM Standards, vol. 03.02, ASTM International, West Conshohocken, PA, 2005.
19. Chaouadi · J. Nucl. Mater. · 2005 · 345 · 6510.1016/j.jnucmat.2005.05.001 ↗
20. G.E. Lucas, G.R. Odette, P. Lombrozo, J.W. Sheckherd, The effects of composition, temperature, and microstructure on the radiation hardening of pressure vessel steels, in: Twelfth International Symposium on the Effects of Irradiation on Materials Effects of Irradiation on Materials, ASTM STP-870, 1985, p. 901.10.1520/STP87019850023 ↗
21. T.J. Williams, P.R. Burch, C.A. English, P.H.N. de la cour Ray,in: G.J. Tbeus, J.R. Weeks (Eds.), Proc. third Int. Symp. on Environmental Degradation of Materials in Nuclear Reactors-Water Reactors, The Metallurgical Society, Warrendale, PA, 1988, p. 121.
22. B.D. Wirth, G.R. Odette, W. Pavinich, G.E. Lucas, S. Spooner, Small angle neutron scattering study of Linde 80 RPV welds, in: Eighteenth International Symposium on the Effects of Radiation on Materials, ASTM STP-1325, ASTM, 1999, p. 102.10.1520/STP13860S ↗
23. ASTM Standard E 900-02, Standard Guide for predicting radiation-induced transition temperature shift in reactor vessel materials, E706 (IIF), Annual Book of ASTM Standards vol. 12.02, American Society for Testing and Materials, West Conshohocken, PA, 2002.
24. Comparison of irradiation-induced shifts of KJc and Charpy impact toughness for reactor pressure vessel steels
25. M.A. Sokolov, R.K. Nanstad, Comparison of irradiation-induced shifts of KJc and Charpy impact toughness for reactor pressure vessel steels, NUREG/CR-6609 (ORNL/TM-13755), USNRC (2001).
26. Reconstitution: where do we stand?
27. ASTM Standard 1253-99, Standard guide for reconstitution of irradiated charpy specimens, Annual Book of ASTM Standards, vol. 12.02, ASTM International, West Conshohocken, PA, 2005.
28. RESQUE: reconstitution techniques qualification & evaluation to study ageing phenomena of nuclear pressure vessel materials
29. M. Scibetta, R. Chaouadi, Effect of reconstitution on fracture toughness measured with PCCv, Report BLG-749, SCK-CEN Mol., Belgium, 1997.
30. Regulatory Guide 1.162, Format and content of report for thermal annealing reactor pressure vessels, US-NRC, 1996.
31. Charpy Embrittlement Correlations – Status of combined mechanistic and statistical bases for US RPV steels (MRP-45), PWR Material Reliability Program (PWRMRP), EPRI, Palo Alto, CA, 2001.
32. Assessment and management of ageing of major nuclear power plant components important to safety: bwr pressure vessels, IAEA TECDOC Series 1470, ISBN 92-0-109305-5, 2005
33. In-service embrittlement of the pressure vessel welds at the Doel I and II nuclear power plants