Phase analysis of hydrogen contained Zr-2.5wt%Nb CANDU pressure tube using plasmon energy loss analysis

Sang-Yeob Lim, SungSoo Kim, Jucheol Park, Gyeong-Geun Lee, Kunok Chang

Publisher page

Abstract

Abstract Canada Deuterium Uranium (CANDU) reactors use Zr-2.5Nb alloys as the pressure tube material. Ensuring optimal performance of Zr-2.5Nb pressure tubes is vital to the safety of CANDU-type heavy water reactors. Long-term use of the pressure tube induces hydrogen pickup and hydride precipitation, causing delayed hydride cracking. Therefore, to evaluate the mechanical integrity of the pressure tube, it is critical to determine the phase distributions inside the pressure tube during hydrogen charging. This study focuses on visually expressing the hydride phasesusingscanning transmission electron microscopy-electron energy loss spectroscopy (STEM-EELS).By using EELS, two phase characterization possibilities were noted at the phase boundary between α-Zr and δ-hydride: nucleated β-Zr and γ-hydride and a mechanical mixture of α-Zr and δ-hydride. The first characterization possibility was reported previously by Barrowet al., and the second possibility is described comprehensively in this paper.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear Materials and Properties · Hydrogen embrittlement and corrosion behaviors in metals · Fusion materials and technologies

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (20)

Show source-provided references
1. Effect of Inhomogeneous Nucleation of Hydride at α/β Phase Boundary on Microstructure Evolution of Zr–2.5 wt% Nb Pressure Tube10.1007/s12540-018-00235-6 ↗
2. Corrosion resistance of titanium, zirconium, and stainless steel10.1021/ie50512a050 ↗
3. Lustman · 1955
4. Nuclear Fuel, Cladding, and the “Discovery” of Zirconium
5. Delayed hydride cracking in Zr–2.5 Nb pressure tube material10.1016/S0022-3115(02)00880-2 ↗
6. Hydrogen concentration limit and critical temperatures for delayed hydride cracking in zirconium alloys10.1016/0022-3115(94)00405-6 ↗
7. Delayed hydride cracking in zirconium alloys in a temperature gradient10.1016/S0022-3115(99)00265-2 ↗
8. Hydrogen analysis in APT: methods to control adsorption and dissociation of H-210.1016/j.ultramic.2013.01.007 ↗
9. Phase and texture analysis of a hydride blister in a Zr–2.5% Nb tube by synchrotron X-ray diffraction10.1016/j.actamat.2010.12.024 ↗
10. The transformation behaviour of the β-phase in Zr–2.5 Nb pressure tubes10.1016/j.jnucmat.2008.08.003 ↗
11. X-ray diffraction studies on asymmetrically broadened peaks of heavily deformed zirconium-based alloys10.1016/j.msea.2007.07.063 ↗
12. EELS characterization of zirconium hydrides10.1051/mmm:019920030103500 ↗
13. A solution to FIB induced artefact hydrides in Zr alloys10.1016/j.jnucmat.2018.12.020 ↗
14. Evaluating zirconium-zirconium hydride interfacial strains by nano-beam electron diffraction10.1016/j.jnucmat.2012.08.003 ↗
15. Savitzky-Golay Smoothing Filters10.1063/1.4822961 ↗
16. Quantitative parameters for the examination of InGaN QW multilayers by low-loss EELS10.1039/C6CP04493J ↗
17. Mapping quantum dot-in-well structures on the nanoscale using the plasmon peak in electron energy loss spectra10.1103/PhysRevB.72.075339 ↗
18. Plasmon peak inhomogeneous broadening in reflection electron energy loss spectroscopy from carbon materials10.1002/sia.2652 ↗
19. Observation of plasmon line broadening in single gold nanorods10.1063/1.2995982 ↗
20. Surface plasmon damping quantified with an electron nanoprobe10.1038/srep01312 ↗