Oxide formation and precipitation behaviors on interface of F82H steel joints during HIPing and hot pressing

Abstract Joining technologies for F82H steels are important issues for the development of fusion energy. The hot isostatic pressing (HIP) method is appropriate for consolidating the first wall of the blanket because of the flexibility of the shape of HIPed products. The HIP method is planned for fabricating a complex-shaped first wall component with built-in cooling channels; thus, accumulation of studies of microstructural and mechanical property changes, especially lower toughness of the HIPed joints, is essential. Present research aims to reveal the microstructural evolution of F82H joints fabricated by the HIP method compared with joints fabricated by hot pressing, focusing on the formation of oxides on the interface. F82H joints were characterized using 1/3-scale Charpy V-notch impact test, transmission electron microscope, scanning electron microscope, and electron probe analysis to survey the microstructural characteristics of the interface.