On the role of alloy composition and processing parameters in nanocluster formation and dispersion strengthening in nanostuctured ferritic alloys
Source abstract
Abstract
Abstract An extensive experimental study characterizing the sequence of events that lead to the formation of a very high density of Y–Ti–O solute nanoclusters (NC) in mechanically alloyed, hot isostatically pressed ferritic stainless steels is reported. Yttria dissolves in the Fe–14Cr–3W(0.4Ti) powders during mechanical alloying. The dissolved Y and O, and when present Ti, subsequently precipitate during hot consolidation. The number densities and volume fractions of the NC decrease, and their radii increase, with increasing consolidation temperature. The NC form at 850 and 1000 °C in milled alloys containing Y, both with and without Ti additions. The presence of Ti refines the NC, and both Ti and high milling energy are necessary for the formation of NC at the highest consolidation temperatures of 1150 °C. However, the precise structure and composition of the NC are not well understood. Indeed, their character varies, depending on the alloy composition and processing variables.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fusion materials and technologies · Nuclear Materials and Properties · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (51)
Show source-provided references
1. Odette · Annu Rev Mater Res · 2008 · 38 · 47110.1146/annurev.matsci.38.060407.130315 ↗
2. FisherJJ, US Patent Number 4,075,010; 1978.
3. Hamilton ML, Gelles DS, Lobsinger RJ, Johnson GD, Brown WF, Paxton M, et al. PNNL-13168 [1991, released 2000].
4. Ukai · J Nucl Mater · 1993 · 204 · 6510.1016/0022-3115(93)90200-I ↗
5. Ukai · J Nucl Sci Technol · 1997 · 34 · 25610.3327/jnst.34.256 ↗
6. Ukai · J Nucl Sci Technol · 1998 · 35 · 29410.3327/jnst.35.294 ↗
7. Ukai · J Nucl Mater · 1998 · 258–263 · 174510.1016/S0022-3115(98)00241-4 ↗
8. Ukai · J Nucl Sci Technol · 1999 · 36 · 71010.3327/jnst.36.710 ↗
9. Ukai · J Nucl Mater · 2000 · 283–287 · 70210.1016/S0022-3115(00)00114-8 ↗
10. Ukai · J Nucl Sci Technol · 2002 · 39 · 87210.3327/jnst.39.872 ↗
11. Ukai · J Nucl Mater · 2002 · 307–311 · 74910.1016/S0022-3115(02)01043-7 ↗
12. Yamashita · Phil Mag Lett · 2004 · 84 · 52510.1080/09500830412331303609 ↗
13. Ohtsuka · J. Phys. Chem. Solids · 2005 · 66 · 57110.1016/j.jpcs.2004.06.033 ↗
14. Sakasegawa · Fusion Eng Des · 2006 · 81 · 101310.1016/j.fusengdes.2005.09.045 ↗
15. Ohtsuka · J Nucl Mater · 2007
16. Okuda · J Mater Sci Lett · 1995 · 14 · 160010.1007/BF00455428 ↗
17. Schaeublin · J Nucl Mater · 2002 · 307–311 · 77810.1016/S0022-3115(02)01193-5 ↗
18. Klimiankou · J Cryst Growth · 2003 · 249 · 38110.1016/S0022-0248(02)02134-6 ↗
19. Klimiankou · J Nucl Mater · 2004 · 329–333 · 34710.1016/j.jnucmat.2004.04.083 ↗
20. Kishimoto · J Nucl Mater · 2004 · 329–333 · 36910.1016/j.jnucmat.2004.04.044 ↗
21. Klimiankou · Micron · 2005 · 36 · 110.1016/j.micron.2004.08.001 ↗
22. Coppola · Physica B · 2004 · 350 · e54510.1016/j.physb.2004.03.148 ↗
23. Yamamoto · J Nucl Mater · 2007
24. Miao · J Nucl Mater · 2007 · 367-370 · 119710.1016/j.jnucmat.2007.03.232 ↗
25. Gelles · J Nucl Mater · 1996 · 233–237 · 29310.1016/S0022-3115(96)00222-X ↗
26. Toloczko · J Nucl Mater · 1998 · 258–263 · 116310.1016/S0022-3115(98)00165-2 ↗
27. Saito · J Nucl Mater · 2000 · 283–287 · 647
28. Yamashita · J Nucl Mater · 2002 · 307–311 · 28310.1016/S0022-3115(02)01077-2 ↗
29. Sagaradze · J Nucl Mater · 2004 · 329–333 · 1053
30. Yamashita · J Nucl Mater · 2004 · 329–333 · 37710.1016/j.jnucmat.2004.04.041 ↗
31. Kishimoto · Fusion Eng Des · 2006 · 81 · 104510.1016/j.fusengdes.2005.09.049 ↗
32. Pareige · J Nucl Mater · 2007 · 360 · 13610.1016/j.jnucmat.2006.09.011 ↗
33. Larson · Scripta Mater · 2001 · 44 · 35910.1016/S1359-6462(00)00593-5 ↗
34. Miller · Mater Sci Eng A – Struct · 2003 · 353 · 14010.1016/S0921-5093(02)00680-9 ↗
35. Miller · J Nucl Mater · 2004 · 329–333 · 33810.1016/j.jnucmat.2004.04.085 ↗
36. Miller · Intermetallics · 2005 · 133–134 · 38710.1016/j.intermet.2004.07.036 ↗
37. Miller · J Nucl Mater · 2006 · 351 · 26110.1016/j.jnucmat.2006.02.004 ↗
38. Alinger · J Nucl Mater · 2004 · 329–333 · 38210.1016/j.jnucmat.2004.04.042 ↗
39. Alinger MJ. On the Formation and Stability of Nanometer Scale Precipitates in Ferritic Alloys during Processing and High Temperature Service. Ph.D. Thesis, University of California, Santa Barbara; 2004.
40. Alamo · J Nucl Mater · 2004 · 329–333 · 33310.1016/j.jnucmat.2004.05.004 ↗
41. Klueh · J Nucl Mater · 2005 · 341 · 10310.1016/j.jnucmat.2005.01.017 ↗
42. Kim · ISIJ Int · 2003 · 43 · 164010.2355/isijinternational.43.1640 ↗
43. JCPDS, Powder Diffraction File, International Center for Diffraction Data, 1601 Park Lane, Swarthmore, PA 19081-2389; 1990.
44. Mizutani · J Am Ceram Soc · 1976 · 59 · 16810.1111/j.1151-2916.1976.tb09459.x ↗
45. Ma · J Appl Phys · 1993 · 74–82 · 95510.1063/1.354837 ↗
46. Kostorz · 1979
47. Mader E. Kinetics of Irradiation Embrittlement and Post-Irradiation Annealing of Nuclear Reactor Pressure Vessel Steels. Ph.D. Thesis, University of California, Santa Barbara; 1995.
48. Miller · 2000
49. Klug · 1974
50. Miao · J Nucl Mater · 2007 · 367–370 · 20810.1016/j.jnucmat.2007.03.144 ↗
51. Miller MK, personal communication.