Investigation of O/M ratio effect on thermal conductivity of oxide nuclear fuels by non-equilibrium molecular dynamics calculation

Abstract The thermal conductivities of UO 2+ x , (U 0.8 ,Pu 0.2 )O 2− x and UO 2 (induced Schottky defects) have been investigated by non-equilibrium molecular dynamics (NEMD) simulation from the viewpoints of the oxygen-to-metal ratio (O/M ratio), temperature, and point defect concentration. In the NEMD simulation, the thermal conductivity was determined by the temperature gradient and heat flux using Fourier’s law. The calculated thermal conductivity decreased with increasing temperature and defect concentration i.e. excess oxygen and oxygen vacancy concentrations. The calculated thermal conductivity decreased with increase of the deviation x from stoichiometry and number of defects. By comparing the hyperstoichiometric and hypostoichiometric oxides, it was found that the effect of Pu 3+ and oxygen vacancy on the thermal conductivity was larger than that of U 5+ and excess oxygen. Further, the cuboctahedral defect clusters were observed in the hyperstoichiometric UO 2+ x supercell.