Superplastic deformation behaviour of friction stir processed 7075Al alloy

Abstract Commercial 7075Al rolled plates were subjected to friction stir processing (FSP) with different processing parameters, resulting in two fine-grained 7075Al alloys with a grain size of 3.8 and 7.5 μm. Heat treatment at 490 °C for 1 h showed that the fine grain microstructures were stable at high temperatures. Superplastic investigations in the temperature range of 420–530 °C and strain rate range of 1×10−3–1×10−1 s−1 demonstrated that a decrease in grain size resulted in significantly enhanced superplasticity and a shift to higher optimum strain rate and lower optimum deformation temperature. For the 3.8 μm 7075Al alloy, superplastic elongations of >1250% were obtained at 480 °C in the strain rate range of 3×10−3–3×10−2 s−1, whereas the 7.5 μm 7075Al alloy exhibited a maximum ductility of 1042% at 500 °C and 3×10−3 s−1. The analyses of the superplastic data for the two alloys revealed a stress exponent of 2, an inverse grain size dependence of 2, and an activation energy close to that for grain boundary self-diffusion. This indicates that grain boundary sliding is the main deformation mechanism for the FSP 7075Al. This was verified by SEM examinations on the surfaces of deformed specimens.