Effects of Heat Treatment on CANDU® Pressure Tube Electrical Resistivity
Source abstract
Abstract
Abstract Material electrical resistivity is an important parameter for eddy current based inspections. For example, material resistivity values for the pressure tube (PT) and calandria tube (CT) are required to ensure accurate measurement of the PT-CT gap in CANDU® reactor fuel channels. Currently, gap measurement calibration is performed on a non-heat treated and non-irradiated PT, and the resistivity used during calibration is assumed to reflect that of in-reactor conditions. In contrast, changes in other parameters that affect gap measurement are compensated using in-reactor measurements. To test whether in-reactor conditions, such as exposure to elevated temperatures, could change a PT material's resistivity, this study examined the effect of heat treatment on Zr-2.5% Nb resistivity. Sectioned PT samples were held for varying periods of time at 400 °C and 450 °C, under anaerobic furnace conditions, in order to partially decompose β-Zr and produce varying fractions of ω-Zr. These temperatures were chosen to accelerate the phase transformations, which take place over a longer period of time under reactor operating conditions, where temperatures are typically between 250 °C and 310 °C. The resistivity of the heat-treated PT samples was measured using the four-point method and changes in resistivity with time at temperature were recorded. The magnitude of the resistivity was observed to decrease by up to 10% after approximately 5000 hrs at 400 °C. Reduction of resistivity with heat treatment was associated with changes in the microstructure and supported by empirical resistivity-microstructure models. Transmission electron microscopy (TEM) showed an increase in the HCP (Hexagonal Closed Packed) ω-phase volume fraction, and an associated decrease in the beta-phase network that was reducing contact between higher conductivity α-Zr grains, which resulted in an overall decrease of resistivity. These results have implications for the uncertainty of PT to CT gap measurement, where temperature variations arise along and around the channel during reactor operations.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear reactor physics and engineering
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (57)
Show source-provided references
1. ENIQ, ENIQ Recommended Practice 1 Influential / Essential Parameters, Luxemburg, 2005.
2. Methods for Evaluation of Accuracy with Multiple Essential Parameters for Eddy Current Measurement of Pressure Tube to Calandria Tube Gap in CANDU® Reactors
3. International Atomic Energy Agency, Assessment and nuclear power plant components management of ageing of major important to safety: CANDU pressure tubes, Vienna, Austria, 1998. https://www-pub.iaea.org/MTCD/Publications/PDF/te_1037_prn.pdf.
4. 2003
5. Canadian Standards Association, N285.4-09 - Periodic Inspection of CANDU Nuclear Power Plant Components, (2009).
6. CSA, Canadian Standards Association Standard CSA N285.4-14, Update No.2, Periodic Inspection of CANDU Nuclear Power Plant Components, Toronto, Canada, 2014.
7. Evolution of Microstructure in Zirconium Alloy Core Components of Nuclear Reactors during Service
8. In-reactor deformation of cold-worked Zr-2.5Nb pressure tubes, J10.1016/j.jnucmat.2007.02.017 ↗
9. Performance of pressure tubes in CANDU reactors10.12943/CNR.2016.00007 ↗
10. Microstructural Aspects of Corrosion and Hydrogen Ingress in Zr-2.5Nb
11. Electrical resistivity and phase transformation in steels10.1002/mawe.200390024 ↗
12. Measurements of electrical resistivity due to phase transformations in indium-rich alloys10.1143/JJAP.24.652 ↗
13. Effect of Low Temperature Irradiation on the Mechanical Properties of V-4Cr-4Ti
14. A Resistometric Study Of The Solution And Precipitation Of Hydrides In Unalloyed Zirconium10.1016/0022-3115(68)90093-7 ↗
15. Electromagnetic evaluation of hydrogen content in Zr 2.5%Nb alloy
16. Estimation of Hydrogen in Zircaloy Using Multi Frequency Eddy Current
17. The transformation behaviour of the β-phase in Zr-2.5Nb pressure tubes10.1016/j.jnucmat.2008.08.003 ↗
18. Evaluation of Concentric Tube Model for Pressure Tube to Calandria Tube Gap Measurement10.1109/JSEN.2019.2909493 ↗
19. S. Contant, G. Klein, J.E. Morelli, T.W. Krause, Inverse Algorithm for Extraction of Multiple Parameters using Analytical Model of Eddy Current Response, IEEE- To Be Publ. (n.d.).
20. Solution for a transmit-receive eddy current probe above a layered planar conductive structure10.1016/j.ndteint.2018.02.003 ↗
21. Klein · 2017
22. Surface profiling with high density eddy current non-destructive examination data10.1016/j.ndteint.2013.12.008 ↗
23. Effects of Extrusion-Billet Preheating on the Microstructure and Properties of Zr-2.5Nb Pressure Tube Materials
24. Recovery of cold-work in extruded Zr-2.5 wt% Nb10.1016/0022-3115(76)90056-8 ↗
25. The Development of Zr-2. 5Nb Pressure Tubes for CANDU Reactors10.1520/JAI103057 ↗
26. A Comparison of X-Ray And Neutron Diffraction Measurement of Lattice Parameters For The Determination of Residual Stress And Chemical Composition In Zirconium Alloy Tubes
27. M. Griffiths, J.E. Winegar, The Transformation Behaviour of the Beta Phase in Zr-2.5 wt% Nb Pressure Tubes, AECL-10835, COG-93-179. (1994).
28. Evolution of Microstructure in Zirconium Alloys During Irradiation
29. Performance Of Pressure Tubes In Candu Reactors10.12943/CNR.2016.00007 ↗
30. G.A. Bickel, M. Griffiths, Manufacturing and microstructure effects on irradiation deformation of Zr-2. 5Nb Pressure Tubing, (2011).
31. Thermal Conductivity, Electrical Resistivity and Specific Heat of CANDU Constructional Zirconium Alloys and AISI Type 403 End Fitting
32. ASTM International, ASTM B193-16- Standard Test Method for Resistivity of Electrical Conductor Materials, (2016) 1–5. doi:10.1520/B0193-02R08.2.
33. I. Keithley Instruments, Model 6220 DC Current Source Model 6221 AC and DC Current Source User ’ s Manual, Cleveland, Ohio, 2005.
34. I. Keithley Instruments, Model 2182 / 2182A Nanovoltmeter User ’ s Manual, Cleveland, Ohio, 2004.
35. Electrical conductivity measurement of metal plates using broadband eddy-current and four-point methods10.1088/0957-0233/16/11/009 ↗
36. Bass · 1982
37. Electrical Conductivity Of Two-Phase Composite Material10.1016/S1359-6462(98)00147-X ↗
38. Electrical Conductivity in Inhomogeneous media
39. K. Tashiro, H. Sedo, M. Ng, Method And Apparatus For Measurement Of Terminal Solid Solublity Temperature In Alloys Capable Of Forming Hydrides, 11/748, 293, 2007. doi:10.1016/j.(73).
40. V.S. Cecco, G. Van Drunen, F.L. Sharp, Eddy Current Testing Manual on Eddy Current Method, Chalk River, Ontario, Canada, 1981. http://www.iaea.org/inis/collection/NCLCollectionStore/_Public/15/061/15061786.pdf (accessed March 31, 2017).
41. V. Cecco, G. Van Drunen, F.L. Sharp, Eddy Current Manual Volume 2 Laboratory Exercises and Demonstrations, (1984). http://cds.cern.ch/record/159737/files/CM-P00067652.pdf.
42. Springer Handbook of Electronic and Photonic Materials
43. Thermodynamic analysis of the stable phases in the Zr-Nb system and calculation of the phase diagram
44. 2000
45. Microsoft 2020, Define and solve a problem by using Solver, (2020). https://support.office.com/en-us/article/define-and-solve-a-problem-by-using-solver-5d1a388f-079d-43ac-a7eb-f63e45925040 (accessed June 1, 2020).
46. Kinetics of phase change. I: General theory10.1063/1.1750380 ↗
47. I. The MathWorks, MATLAB, (n.d.). https://www.mathworks.com/products/matlab.html (accessed December 7, 2017).
48. The transformation and age hardening behaviour of Zr-19 WT% Nb10.1016/0022-3115(73)90109-8 ↗
49. A review of microstructure evolution in zirconium alloys during irradiation10.1016/0022-3115(88)90093-1 ↗
50. L. Balogh, F. Long, T. Lucas, D. Brown, B. Clausse, T. Sisneros, A. Barry, M.R. Daymond, Quantifying the recovery of irradiation defects and cold work in Zr-2.5% Nb using diffraction, Prep. (n.d.).
51. The stability of precipitates in an irradiation environment10.1016/0022-3115(72)90043-8 ↗
52. G.A. Bickel, M. Griffiths, H. Chaput, A. Buyers, C.E. Coleman, Modeling Irradiation Damage in Zr-2.5Nb and Its Effects on Delayed Hydride Cracking Growth Rate, in: B. Comstock (Ed.), Zircon. Nucl. Ind. 17th Vol., 2015: pp. 800–829. doi:10.1520/STP154320120157.10.1520/STP154320120157 ↗
53. Modelling and validation of Eddy current response to changes in factors affecting pressure tube to calandria tube gap measurement10.1016/j.ndteint.2015.02.005 ↗
54. Methods For Evaluation Of Accuracy With Multiple Essential Parameters For Eddy Current Measurement Of Pressure Tube To Calandria Tube Gap In CANDU® Reactors
55. Understanding the mechanics of creep deformation to develop a surrogate model for contact assessment in CANDU® fuel channels10.1016/j.nucengdes.2018.01.032 ↗
56. Luloff · 2016
57. Shokralla · 2016