The microstructure of laser welded V–4Cr–4Ti alloy after neutron irradiation
Source abstract
Abstract
Abstract Effects of neutron irradiation on YAG laser welded V–4Cr–4Ti alloy were studied in JMTR (Japanese Materials Testing Reactor). The samples with and without post-weld heat treatment (PWHT) at 1073 K were irradiated in the temperature range of 673–873 K up to the dose of 0.45 dpa. After the irradiation, the microstructure and Vickers hardness of the welded samples were compared of the base metal, which were simultaneously irradiated at the same irradiation cycle.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fusion materials and technologies · Hydrogen embrittlement and corrosion behaviors in metals · Nuclear Materials and Properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (8)
Show source-provided references
1. Muroga · J. Nucl. Mater. · 2002 · 307–311 · 54710.1016/S0022-3115(02)01253-9 ↗
2. Grossbeck · J. Nucl. Mater. · 2002 · 307–311 · 159010.1016/S0022-3115(02)00968-6 ↗
3. Nagasaka · J. Nucl. Mater. · 2002 · 307–311 · 159510.1016/S0022-3115(02)01170-4 ↗
4. Heo · Fusion Sci. Technol. · 2003 · 44 · 47010.13182/FST03-A380 ↗
5. Watanabe · Mater. Sci. Forum · 2005 · 475–479 · 149110.4028/www.scientific.net/MSF.475-479.1491 ↗
6. Nagasaka · J. Nucl. Mater. · 2004 · 329–333 · 153910.1016/j.jnucmat.2004.04.171 ↗
7. Muroga · J. Nucl. Mater. · 2000 · 283–287 · 71110.1016/S0022-3115(00)00281-6 ↗
8. Nam-Jin Heo, T. Nagasaka, T. Muroga, A. Nishimura, K. Sinozaki, H. Watanabe, J. Nucl. Mater., submitted for publication.