He and H irradiation effects on the nanoindentation hardness of CLAM steel

Abstract In this study, He and H ion irradiation induced hardening behavior of China Low Activation Martensitic (CLAM) steel was investigated, and the influence of Si on irradiation hardening was also examined. CLAM steel with different Si contents, Heat 0912 and Heat 0408D, were irradiated with single He (He concentration range from 0 to 2150 appm) ion beam and He/H dual ion beams. Then nanoindentation tests were applied to evaluate the ion irradiation induced hardening effect. The result of Heat 0912 showed hardening effect would be more serious with higher He concentration, and the trend saturated when He concentration reach 1000 appm. Comparing the result of Heat 0912 and Heat 0408D, higher Si content might improve the resistance to hardening.