Modification of tungsten layers by arcing

Numerous traces of arcs have been found on W-covered graphite tiles of ASDEX Upgrade after exposure. The distributions of number density, lengths and orientation are calculated and compared to pure graphite tiles at comparable locations. It was established that arcs perforate a 1 μm tungsten layer down to the carbon substrate. The amount of removal should rise with arc current, but a surface fraction of about 8% is eroded at 10 A already. At tiles of the divertor baffle the layer is continuously removed along the entire track pointing to higher currents. The carbon of the stripped parts is subject to subsequent erosion processes. The distribution of materials in and around arc tracks was investigated by sputter depth profiling (SIMS and AES) and the characteristic geometry was studied using an electron microscope. Observations are interpreted using results from laboratory vacuum arcs on the same material.