Stability of 3-D carbon fiber composite to high neutron fluence

Abstract The dimensional stability, elastic modulus, and flexural strength of a high quality, three-dimensional balanced weave carbon fiber composite has been evaluated over a range of neutron fluence to ∼32 dpa at ∼800 °C. Results indicate that while the composite exhibits continuous strengthening over this dose range, this occurs with measurable loss of mass, increased volume, and for the highest dose studied, a large reduction in elastic modulus. While the balanced-weave composite was orthogonally isotropic, a significant anisotropic dimensional change occurred under irradiation. Dimensional change was dominated by fiber dimensional change and the overall shrinkage or swelling in a direction was determined by the extent to which intrinsic fiber shrinkage was capable of restraining swelling of matrix and fiber bundles.