Hydrogen concentrations near cracks in target materials for high-power spallation neutron sources
Source abstract
Abstract
Abstract Materials in the target region of spallation neutron sources which are exposed, or are close to the proton beam suffer from high rates of displacement damage and the production of foreign elements, particularly hydrogen and helium isotopes. Whilst some results on the effect of helium are now available, there is little information on the potential influence of hydrogen in the environment of a spallation source. We therefore investigate theoretically the establishment of hydrogen background concentrations and their enhancement near microcracks in proton-irradiated plates of ferritic/martensitic steel and tantalum, respectively, for the conditions of the envisaged 5 MW European Spallation Source (ESS). A comparison of the predicted hydrogen concentrations with empirical threshold concentrations for hydrogen embrittlement and hydride formation indicates that the use of ferritic/martensitic steels for water-cooled windows may be problematic, although these materials remain good candidates for the mercury container. Tantalum as a prospective material for the solid target option of ESS is not expected to undergo hydrogen degradation.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Nuclear Materials and Properties · Fusion materials and technologies · Nuclear Physics and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (46)
Show source-provided references
1. H. Lengeler, in: Proc. 13th Meeting of International Collaboration on Advanced Neutron Sources, PSI Report, Villingen, 1995, p. 819
2. J. Kjems, in: A New Generation Neutron Source for Europe, vol. III, ESS Technical Study, Roskilde, 1997, p. 4
3. Ullmaier · Nucl. Instrum. and Meth. B · 1995 · 101 · 40610.1016/0168-583X(95)00590-0 ↗
4. Ullmaier · Mater. Sci. Forum · 1992 · 97–99 · 45110.4028/www.scientific.net/MSF.97-99.451 ↗
5. L.K. Mansur, H. Ullmaier (Eds.), Proc. Int. Workshop on Spallation Materials Technology, ORNL Report, Oak Ridge, TN, 1996
6. Hirth · Acta Metall. · 1978 · 26 · 179510.1016/0001-6160(78)90092-5 ↗
7. Hirth · Metall. Trans. · 1980 · 11A · 86110.1007/BF02654700 ↗
8. Kirchheim · Scr. Metall. · 1982 · 16 · 47510.1016/0036-9748(82)90176-4 ↗
9. J.P. Hirth, in: R.A. Oriani, J.P. Hirth, M. Smialowski (Eds.), Hydrogen Degradation of Ferrous Alloys, Noyes, Park Ridge, NJ, 1985, p. 131
10. Rauh · Proc. R. Soc. London A · 1985 · 397 · 12110.1098/rspa.1985.0007 ↗
11. Rauh · Proc. R. Soc. London A · 1990 · 427 · 110.1098/rspa.1990.0001 ↗
12. H. Rauh, in: K.P. Herrmann, Z.S. Olesiak (Eds.), Thermal Effects in Fracture of Multiphase Materials, Springer, Berlin, 1990, p. 4610.1007/978-3-642-88479-5_5 ↗
13. D. Filges, R.D. Neef, H. Schaal, A. Tietze, U. Weber, W. Breuer, J. Wimmer (Eds.), Damage Studies for Structure and Beam Window Materials for the ESS Mercury Target, ESS Report, Jülich, 1996
14. Green · J. Nucl. Mater. · 1988 · 155–157 · 135010.1016/0022-3115(88)90525-9 ↗
15. D. Filges, C. Mayer, R.D. Neef, H. Schaal, A. Tietze, J. Wimmer (Eds.), Development of Cross Sections for Materials Damage and Helium Production for ESS, ESS Report, Jülich, 1996
16. Schroeder · Z. Phys. B · 1976 · 25 · 9110.1007/BF01343313 ↗
17. Wedig · J. Nucl. Mater. · 1997 · 245 · 13810.1016/S0022-3115(97)00014-7 ↗
18. Forcey · J. Nucl. Mater. · 1997 · 240 · 11810.1016/S0022-3115(96)00670-8 ↗
19. Schaumann · Phys. Status Solidi · 1970 · 42 · 40110.1002/pssb.19700420141 ↗
20. Heumann · 1992 · 220
21. Rauh · Philos. Mag. A · 1992 · 65 · 5310.1080/01418619208201479 ↗
22. Hobson · J. Iron Steel Inst. · 1959 · 191 · 342
23. R. Boler, C.B.A. Forty, G.J. Butterworth, in: An Initial Examination of the Likely Effect of Hydrogen on Low Activation Martensitic Steel, AEA Report, Culham, 1992, p. 3
24. M.P. Puls, in: R.A. Oriani, J.P. Hirth, M. Smialowski (Eds.), Hydrogen Degradation of Ferrous Alloys, Noyes, Park Ridge, NJ, 1985, p. 114
25. McMullen · Philos. Mag. A · 1989 · 59 · 16110.1080/01418618908220336 ↗
26. T. Schober, H. Wenzl, in: G. Alefeld, J. Völkl (Eds.), Hydrogen in Metals II, Springer, Berlin, 1978, p. 1110.1007/3-540-08883-0_18 ↗
27. Schober · J. Phys. F · 1988 · 18 · 111910.1088/0305-4608/18/6/015 ↗
28. Rauh · Proc. R. Soc. London A · 1983 · 388 · 31110.1098/rspa.1983.0085 ↗
29. H.P. van Leeuwen, in: R.A. Oriani, J.P. Hirth, M. Smialowski (Eds.), Hydrogen Degradation of Ferrous Alloys, Noyes, Park Ridge, NJ, 1985, p. 16
30. H. Borchers, H. Hausen, K.H. Hellwege, K. Schäfer, E. Schmidt (Eds.), Landolt-Börnstein, Zahlenwerte und Funktionen aus Physik, Chemie, Astronomie, Geophysik und Technik, N.S., vol. II/1, Springer, Berlin, 1971, p. 298
31. Beattie · Proc. Am. Acad. Arts Sci. · 1928 · 63 · 29910.2307/20026205 ↗
32. Heinrich · J. Electrochem. Soc. · 1965 · 112 · 106710.1149/1.2423362 ↗
33. Ali-Khan · J. Nucl. Mater. · 1978 · 74 · 132 and 13810.1016/0022-3115(78)90542-1 ↗
34. Broek · 1991 · 94
35. Gross · 1996 · 96
36. G. Leibfried, N. Breuer, Point Defects in Metals I, Springer, Berlin, 1978, pp. 189 and 227
37. Magerl · Phys. Status Solidi (a) · 1976 · 36 · 16110.1002/pssa.2210360117 ↗
38. Sutton · 1995 · 436
39. Bai · Metall. Trans. · 1994 · 25A · 118510.1007/BF02652293 ↗
40. H.G. Nelson, in: M.R. Louthan, R.P. McNitt, R.D. Sisson (Eds.), Proc. Conf. on Environmental Degradation of Engineering Materials, vol. III, Pennsylvania State University, University Park, PA, 1987, p. 83
41. Jung · Fus. Technol. · 1998 · 33 · 6310.13182/FST98-A16 ↗
42. Forcey · J. Nucl. Mater. · 1988 · 160 · 11710.1016/0022-3115(88)90038-4 ↗
43. Ullmaier · J. Nucl. Mater. · 1997 · 251 · 26210.1016/S0022-3115(97)00226-2 ↗
44. Nejedlik · Corrosion · 1964 · 20 · 25010.5006/0010-9312-20.12.384t ↗
45. T. Schober, in: F.A. Lewis, A. Aladjem (Eds.), Hydrogen Metal Systems I, Scitec, Uetikon, 1996, pp. 357 and 423
46. T. Broome, private communication