Thermal expansion studies on UMoO5, UMoO6, Na2U(MoO4)3 and Na4U(MoO4)4

Abstract In the present work, thermal expansion behavior of lower valent sodium uranium molybdates, i.e., Na 2 U(MoO 4 ) 3 and Na 4 U(MoO 4 ) 4 were studied under vacuum in the temperature range of 298–873 K using high temperature X-ray diffractometry (HTXRD). Expansion behaviors of UMoO 5 and UMoO 6 were also studied in vacuum from 298 to 873 K and 773 K, respectively. UMoO 5 was synthesized by reacting UO 2 with MoO 3 in equi-molar proportion in evacuated sealed quartz ampoule at 1173 K for 14 h. Na 2 U(MoO 4 ) 3 and Na 4 U(MoO 4 ) 4 were prepared by reacting UMoO 5 and MoO 3 with 1 and 2 moles of Na 2 MoO 4 , respectively, at 873 K in evacuated sealed quartz ampoule. XRD data of UMoO 5 and UMoO 6 were indexed on orthorhombic and monoclinic systems, respectively, whereas, the data of Na 2 U(MoO 4 ) 3 and Na 4 U(MoO 4 ) 4 were indexed on tetragonal system. The lattice parameters and cell volume of all the four compounds, fit into polynomial expression with respect to temperature, showed positive thermal expansion (PTE) up to 873 K.