Mechanical properties of neutron-irradiated vanadium alloys in a liquid-sodium environment

Abstract Vanadium alloys, including the highly purified V-4Cr-4Ti alloy called NIFS-Heat2, in the form of sodium-enclosed irradiation capsules, were irradiated up to a damage level of 5 dpa in the Joyo reactor at temperatures from 395 to 601 °C. An increase of the ductile – brittle transition temperature (DBTT) by neutron irradiation and irradiation hardening were observed. No significant loss of ductility was observed even for irradiation at 395 and 450 °C. The addition of titanium to V-Cr alloys was effective for irradiation hardening at high temperature. Hydrogen uptake in the cleaning process during dismantling of the irradiation capsules caused ductility loss of the highly purified V-4Cr-4Ti alloys; the alloys recovered their ductility when they were annealed at 400 °C in vacuum. The uniform formation of Ti(OCN) precipitate was suppressed in highly purified V-4Cr-4Ti alloys irradiated in Joyo in a liquid-sodium environment.