Radiation-induced segregation in desensitized type 304 austenitic stainless steel

Abstract Radiation-induced segregation (RIS) in desensitized type 304 stainless steel (SS) was investigated using a combination of electrochemical potentiokinetic reactivation (EPR) test and atomic force microscopy (AFM). Desensitized type 304 SS was irradiated to 0.43 dpa (displacement per atom) using 4.8 MeV protons at 300 °C. The maximum attack in the EPR test for the irradiated desensitized SS was measured at a depth of 70 μm from the surface. Grain boundaries and twin boundaries got attacked and pit-like features within the grains were observed after the EPR test at the depth of 70 μm. The depth of attack, as measured by AFM, was higher at grain boundaries and pit-like features as compared to twin boundaries. It has been shown that the chromium depletion due to RIS takes place at the carbide–matrix as well as at the carbide–carbide interfaces at grain boundaries. The width of attack at grain boundaries after the EPR test of the irradiated desensitized specimen appeared larger due to the dislodgement of carbides at grain boundaries.