Detection of intergranular cracking susceptibility due to hydrogen in irradiated austenitic stainless steel with a superconducting quantum interference device (SQUID) sensor

Abstract To investigate the detection method of intergranular (IG) cracking susceptibility by hydrogen in irradiated austenitic stainless steel (SS), magnetic and mechanical properties were examined after two repeats of hydrogen charging and discharging (hydrogen treatment) in Type 304 SS which had been irradiated during use in different reactor cores. The residual magnetic flux density (Br) was measured with a superconducting quantum interference device sensor and Br increased with increased neutron fluence and repeated hydrogen treatments. Elongation decreased with an increase of Br and IG cracking appeared above Br of 2×10−5 T for this measuring method after repeated hydrogen treatments. These phenomena would be caused by hydrogen-induced martensite phase being formed on grain boundaries. It was thought the appearance of IG cracking susceptibility due to hydrogen in irradiated SS could be predicted by measuring the Br of the steel.