Understanding long-term corrosion of Alloy 22 container in the potential Yucca Mountain repository for high-level nuclear waste disposal

Abstract Alloy 22 (Ni–22Cr–13Mo–3W–4Fe) is the candidate material for the waste package outer container in a potential geologic repository for high-level nuclear waste disposal at Yucca Mountain, Nevada. This alloy exhibits very low corrosion rates in the absence of environmental conditions promoting crevice corrosion. However, there are uncertainties regarding Alloy 22’s corrosion performance when general corrosion rates and susceptibility to crevice corrosion are extrapolated to a geological time period (e.g. 105 years). This paper presents an analysis of available literature information relevant to the long-term extrapolation of general corrosion processes and the crevice corrosion behavior of Alloy 22, under potential repository environments. For assessment of general corrosion rates, potential degradation processes causing the loss of the long-term persistence of passive film formed are considered. For crevice corrosion, induction time, and the extent of susceptibility and opening area, are considered. Disclaimer: The US Nuclear Regulatory Commission (NRC) staff views expressed herein are preliminary and do not constitute a final judgment or determination of the matters addressed nor of the acceptability of a license application for a geologic repository at Yucca Mountain. The paper describes work performed by the Center for Nuclear Waste Regulatory Analyses (CNWRA) for NRC under Contract Number NRC-02-02-012. The activities reported here were performed by CNWRA on behalf of the NRC office of Nuclear Material Safety and Safeguards, Division of High Level Waste Repository Safety. This paper is an independent product of the CNWRA and does not necessarily reflect the view or regulatory position of the NRC.