In situ tailoring microstructure in additively manufactured Ti-6Al-4V for superior mechanical performance
Source abstract
Abstract
Abstract The “Holy Grail” of metal additive manufacturing is to manufacture reliable high-performance metal parts with no or a minimal need of post processing. However, Ti-6Al-4V parts made by selective laser melting (SLM) often suffer from poor ductility and low toughness because of the predominant acicular α′ martensite contained in columnar prior-β grains. In practice, post heat treatment is necessary. To overcome this deficiency, we have explored designing innovative SLM processing routes to turn the unfavoured α′ martensite, via in-situ decomposition, into lamellar (α+β) microstructures with tuneable characteristic length scales. Such lamellar (α+β) microstructures lead to superior mechanical properties which markedly exceed ASTM standards and outperform the majority of Ti-6Al-4V fabricated by other additive manufacturing processes. Furthermore, we find that the lattice parameter of the β phase in the (α+β) lamellae falls into a specific range of 3.18–3.21 A. Hence the lattice parameter of β phase can serve as an indicator to predict whether significant martensite decomposition has taken place in situ in Ti-6Al-4V made by SLM. This work marks an important step forward in the understanding of how to tailor microstructure in situ for the development of high-performance Ti-6Al-4V parts by SLM.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Additive Manufacturing Materials and Processes · Additive Manufacturing and 3D Printing Technologies · Welding Techniques and Residual Stresses
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. A study of the micro structural evolution during selective laser melting of Ti-6Al-4V10.1016/j.actamat.2010.02.004 ↗
2. The metallurgy and processing science of metal additive manufacturing10.1080/09506608.2015.1116649 ↗
3. Selective laser melting of biocompatible metals for rapid manufacturing of medical parts10.1108/13552540710776142 ↗
4. Ductility of a Ti-6Al-4V alloy produced by selective laser melting of prealloyed powders10.1108/13552541011083371 ↗
5. As-fabricated and heat-treated microstructures of the Ti-6Al-4V alloy processed by selective laser melting, Metall10.1007/s11661-011-0731-y ↗
6. Metal additive manufacturing: a review of mechanical properties10.1146/annurev-matsci-070115-032024 ↗
7. Critical assessment of the fatigue performance of additively manufactured Ti-6Al-4V and perspective for future research10.1016/j.ijfatigue.2015.12.003 ↗
8. Additive manufacturing of strong and ductile Ti-6Al-4V by selective laser melting via in-situ martensite decomposition10.1016/j.actamat.2014.11.028 ↗
9. Heat treatment of Ti6Al4V produced by selective laser melting: microstructure and mechanical properties10.1016/j.jallcom.2012.07.022 ↗
10. Microstructural control of additively manufactured metallic materials10.1146/annurev-matsci-070115-031816 ↗
11. On the texture formation of selective laser melted Ti-6Al-4V10.1007/s11661-014-2218-0 ↗
12. Additive manufacturing and post-processing of Ti-6Al-4V for superior mechanical properties10.1557/mrs.2016.215 ↗
13. Additive manufacturing of metals10.1016/j.actamat.2016.07.019 ↗
14. Ti-6Al-4V additively manufactured by selective laser melting with superior mechanical properties10.1007/s11837-015-1297-8 ↗
15. Understanding the microstructure formation of Ti-6Al-4V during direct laser deposition via in-situ thermal monitoring10.1007/s11837-015-1767-z ↗
16. The laser additive manufacture of Ti-6Al-4V10.1007/s11837-001-0068-x ↗
17. The origin of microstructural diversity, texture, and mechanical properties in electron beam melted Ti-6Al-4V10.1007/s11661-010-0397-x ↗
18. Microstructure and mechanical properties of long Ti-6Al-4V rods additively manufactured by selective electron beam melting out of a deep powder bed and the effect of subsequent hot isostatic pressing, Metall10.1007/s11661-015-2976-3 ↗
19. Influence of tempering temperature and time on the alpha'-Ti-6Al-4V martensite10.1016/0925-8388(95)02057-8 ↗
20. Kinetics of martensite decomposition in Ti-6Al-4V-xH alloys10.1016/S0921-5093(03)00350-2 ↗
21. Boyer · 1994
22. In situ observations of lattice expansion and transformation rates of alpha and beta phases in Ti-6Al-4V10.1016/j.msea.2004.08.084 ↗
23. Columnar to equiaxed grain transition in as solidified alloys10.1179/174328006X102493 ↗
24. Hall-Petch relation and boundary strengthening10.1016/j.scriptamat.2004.06.002 ↗
25. Effect of powder reuse times on additive manufacturing of Ti-6Al-4V by selective electron beam melting10.1007/s11837-015-1300-4 ↗
26. On the fatigue properties of metals manufactured by selective laser melting - the role of ductility10.1557/jmr.2014.157 ↗
27. Evaluation of microstructural development in electron beam melted Ti-6Al-4V10.1016/j.matchar.2011.12.008 ↗
28. Microstructure and mechanical properties of Ti-6Al-4V produced by electron beam melting of pre-alloyed powders10.1108/13552540910960262 ↗
29. Graded microstructure and mechanical properties of additive manufactured Ti-6Al-4V via electron beam melting10.1016/j.actamat.2015.06.036 ↗
30. Microstructures and mechanical properties of Ti6Al4V parts fabricated by selective laser melting and electron beam melting10.1007/s11665-013-0658-0 ↗