Effect of periodic temperature variations on the microstructure of neutron-irradiated metals
Source abstract
Abstract
Abstract Specimens of pure copper, a high purity austenitic stainless steel, and V–4Cr–4Ti were exposed to eight cycles of either constant temperature or periodic temperature variations during neutron irradiation in the High Flux Isotopes Reactor to a cumulative damage level of 4–5 displacements per atom. Specimens exposed to periodic temperature variations experienced a low temperature (360 °C) during the initial 10% of accrued dose in each of the eight cycles, and a higher temperature (520 °C) during the remaining 90% of accrued dose in each cycle. The microstructures of the irradiated stainless steel and V–4Cr–4Ti were qualitatively similar to companion specimens that were continuously maintained at 520 °C during the entire irradiation. The microstructural observations on pure copper irradiated at a constant temperature of 340 °C in this experiment are also summarized. The main radiation-induced microstructural features consisted of dislocation loops, stacking fault tetrahedra and voids in the stainless steel, Ti-rich precipitates in the V alloy, and voids (along with a low density of stacking fault tetrahedra) in copper.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Fusion materials and technologies · Nuclear Materials and Properties · Hydrogen embrittlement and corrosion behaviors in metals
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. Kiritani · J. Nucl. Mater. · 1988 · 160 · 13510.1016/0022-3115(88)90040-2 ↗
2. Kiritani · J. Nucl. Mater. · 1990 · 174 · 32710.1016/0022-3115(90)90245-I ↗
3. Kiritani · J. Nucl. Mater. · 1991 · 179–181 · 110410.1016/0022-3115(91)90285-F ↗
4. Kiritani · J. Nucl. Mater. · 1994 · 212–215 · 24110.1016/0022-3115(94)90064-7 ↗
5. Yoshida · J. Nucl. Mater. · 1994 · 212–215 · 47110.1016/0022-3115(94)90106-6 ↗
6. Xu · J. Nucl. Mater. · 1994 · 212–215 · 25810.1016/0022-3115(94)90067-1 ↗
7. Matsui · J. Nucl. Mater. · 1994 · 212–215 · 78410.1016/0022-3115(94)90163-5 ↗
8. Xu · J. Nucl. Mater. · 1996 · 233–237 · 105710.1016/S0022-3115(96)00118-3 ↗
9. Muroga · J. Nucl. Mater. · 1998 · 258–263 · 13010.1016/S0022-3115(98)00266-9 ↗
10. Ochiai · J. Nucl. Mater. · 1999 · 271&272 · 37610.1016/S0022-3115(98)00751-X ↗
11. Yoshida · J. Nucl. Mater. · 1992 · 191–194 · 111410.1016/0022-3115(92)90648-5 ↗
12. Zinkle · J. Nucl. Mater. · 1993 · 206 · 26610.1016/0022-3115(93)90128-L ↗
13. Horiki · J. Nucl. Mater. · 1996 · 239 · 3410.1016/S0022-3115(96)00472-2 ↗
14. Rice · J. Nucl. Mater. · 1998 · 258–263 · 141410.1016/S0022-3115(98)00208-6 ↗
15. Zinkle · Radiat. Eff. Def. Solids · 1999 · 148 · 44710.1080/10420159908229104 ↗
16. A.L. Qualls, T. Muroga, in: Fusion Materials Semiannual Progress Report for Period ending 30 June 2000, DOE/ER-0313/28, Oak Ridge National Lab., 2000, p. 266
17. D.T. Hoelzer, S.J. Zinkle, in: Fusion Materials Semiannual Progress Report for Period ending 31 December 2000, DOE/ER-0313/29, Oak Ridge National Lab., 2000, p. 19
18. Zinkle · J. Nucl. Mater. · 1989 · 168 · 26210.1016/0022-3115(89)90591-6 ↗
19. Zinkle · J. Nucl. Mater. · 1991 · 168 · 26210.1016/0022-3115(89)90591-6 ↗
20. Mazey · J. Nucl. Mater. · 1988 · 154 · 18610.1016/0022-3115(88)90354-6 ↗
21. Nita · J. Nucl. Mater. · 1999 · 271&272 · 376
22. Muroga · J. Nucl. Mater. · 2001 · 299 · 14810.1016/S0022-3115(01)00675-4 ↗