Analyses of erosion and re-deposition layers on graphite tiles used in the W-shaped divertor region of JT-60U

Erosion and re-deposition profiles were studied on graphite tiles used in the W-shaped divertor of JT-60U in June 1997-October 1998 periods, operated with all-carbon walls with boronizations and inner-private flux pumping. Continuous re-deposition layers were found neither on the dome top nor on the outer wing, while re-deposition layers of around 20 pm thickness were found on the inner wing, in the region close to the dome top. On the outer divertor target, erosion was found to be dominant: maximum erosion depth of around 20 μm was measured, while on the inner target, re-deposition was dominant: columnar structure layers of maximum thickness at around 30 pm on the inner zone while laminar/columnar-layered structures of maximum thickness around 60 μm were found on the outer zone. Poloidal distributions of the erosion depth/re-deposition layer thickness were well correlated with the frequency histograms of strike point position, which were weighted with total power of neutral beam injection, on both the outer and inner targets. Through X-ray photoelectron spectroscopy, composition of the re-deposition layers at a mid zone on the inner target were 3-4 at.% B and <0.6 at.% O, Fe, Cr, and Ni with remaining C. Boron atoms are mostly bound to C atoms but some may precipitated as boron.