Micro-tensile characteristics of As-fabricated and irradiated AGR-2 TRISO fuel particle buffer, IPyC, and buffer-IPyC interlayer regions

A recently developed micro-tensile sample preparation technique was implemented to evaluate the tensile strengths of the buffer, IPyC, and buffer-IPyC interlayer regions of the unirradiated and irradiated AGR-2 TRISO fuel particles. Understanding the mechanical properties of the buffer-IPyC interlayer is essential for developing thermomechanical models of buffer-IPyC separation, yet there is a lack of experimental data on its micro-tensile properties. TEM analysis was conducted on these regions to determine the microstructural changes relevant to the samples' tensile properties. In the unirradiated TRISO particle samples, the buffer layer demonstrated the weakest tensile strength, while the IPyC layer exhibited the highest. Conversely, in the irradiated TRISO particle samples, the buffer-IPyC interlayer region showed the lowest tensile strength, with the IPyC layer being the strongest. Fractures in the samples from the buffer-IPyC region predominantly occurred either in the buffer layer or at the buffer-IPyC interface. However, some buffer-IPyC interlayer samples displayed stress-strain and fracture behaviors more akin to the IPyC layer than the buffer layer. Analysis of diffraction patterns suggests that irradiation may have increased anisotropy in the three regions tested. Despite this suggested increase in anisotropy, there was no evidence that it affected the measured strengths. The irradiated TRISO particles demonstrated a considerable increase in void space and a decrease in ultimate tensile strength within the buffer-IPyC interlayer region due to the densification and contraction of the buffer layer. Minor variations in diffraction ring patterns were also observed. These changes, coupled with a significant reduction in the Weibull modulus/shape parameter, imply that irradiation-induced densification leads to tearing between the buffer and IPyC layers at locations of elevated porosity in the buffer-IPyC interlayer region.